High strength medium wall quenched and tempered seamless steel pipes and related method for manufacturing said steel pipes

ABSTRACT

Disclosed herein are embodiments of a seamless quenched and tempered steel pipe which can have a wall thickness WT higher than or equal to 6 mm and lower than or equal to 35 mm. Some embodiments of the steel pipe can have a chemical composition comprising C, Mn, Si, Cr, Ni, Mo, Al, N, Ca, Nb, Ti, V, Zr, and Ta based on the composition weight, the remaining being iron and impurities. In some embodiments, wherein (V+Nb) content is lower than 0.07 wt %; defining a first parameter P1=(60×C)+Cr+[5×e (35×Mo/WT) ]+50×(V+Nb), the chemical composition satisfies a first condition P1≦14.5.

INCORPORATION BY REFERENCE TO ANY PRIORITY APPLICATIONS

Any and all applications for which a foreign or domestic priority claim is identified in the Application Data Sheet as filed with the present application are hereby incorporated by reference under 37 CFR 1.57.

BACKGROUND

Field

The present disclosure in certain embodiments relates to medium wall seamless steel pipes having a wall thickness (WT) higher than or equal to 6 mm and lower than or equal to 35 mm, and in certain embodiments relates also to a method for manufacturing the seamless steel pipes. Said seamless steel pipes, suitable for linepipes, flowlines and risers for use in the oil and gas industry, can also include pipes that are suitable for hot bending.

Description of the Related Art

Exploration of offshore oil and gas reserves in remote regions of the world is increasingly moving away from conditions where relatively traditional pipe solutions can be utilized and towards more demanding environments. These more demanding environments may incorporate a combination of very challenging factors including, for example, deepwater locations, increased pressure and temperature wells, more corrosive products, and lower design temperatures. These conditions, when added to stringent weldability and toughness criteria already associated with pipe specifications for offshore oil and gas exploration applications, place ever increasing demands on the materials and supply capability.

These demands are evident in project developments involving aggressive environment and high operating pressure. For example, major seamless linepipe manufacturers are able to manufacture pipes of grades X60, X65 and X70 according with American Petroleum Institute (API) 5L and International Organization for Standards (ISO) 3183 standards, with sulfide stress corrosion (SSC) and hydrogen induced cracking (HIC) resistance. However, the strength and toughness trade-off, combined with the need for sulfide stress corrosion (SSC) and hydrogen induced cracking (HIC) resistance (e.g., sour resistance) have been proven difficult to achieve. In particular, quenched and tempered (Q&T) seamless pipes of API 5L grade X60, X65 and X70 typically exhibit maximum hardness values, measured at 1.5-2.0 mm depth from the pipe surfaces (according to API 5L-ISO 3183), below 250 HV₁₀ but however above 235HV₁₀, whereas now new projects require lower values to make the material weldable and resistant to SSC as per Region 3 in NACE MR-0175. These lower maximum hardness values cannot be consistently achieved with current steel chemical compositions and processes.

Moreover, pipelay operations, especially when linepipes are installed by means of the reel laying method, cause repeated plastic bending and straightening deformation cycles. These cyclic loads, producing both cold working and Bauschinger effect, may affect final material stress-strain properties.

Reeling is currently applied to an increasing range of pipe geometries, being the present limit given by pipes with 16″ outside diameter (OD) and 35 mm wall thickness (WT). Other pipeline installation techniques, for example, J-lay, S-lay and steep S-lay also introduce plastic strain.

Accumulated plastic strain, combined with ageing, can reduce the ductility and toughness of the pipe material. Therefore, strain ageing and toughness tests must be carried out following specified procedures when the pipeline is to be exposed to more than 2% plastic strain during installation (as prescribed by DNV OS-F101, 2012). Plastic deformation of the pipe may also decrease the resistance to sulfide stress corrosion cracking, but it is commonly assumed that if traditional safe hardness levels are maintained after straining, there will be sufficient control over the risk of sulfide stress cracking in service.

In the past years, there have been several types of high-strength linepipe steels developed in the field of Q&T seamless pipes. These seamless pipes combine both strength and good girth weldability. However, these seamless pipes exhibit chemical compositions which hinder hardness reduction during tempering. Therefore, close to pipe surface, where very high cooling rates are experienced during external and internal water quenching and high hardness values are obtained after quenching due to formation of a predominant martensitic microstructure, the risk exists that, even after tempering at high temperature and long time, the maximum hardness values along the whole wall thickness of the pipe remain above 235 HV₁₀ and less preferably above 240 HV₁₀.

The alloying concept applied to Q&T seamless pipes of grade X65/X70 by some seamless line pipe manufacturers is based on microalloying with Vanadium and niobium. However, individual hardness values are not systematically below or equal to 235 HV₁₀ along the whole wall thickness.

Moreover, in the case of hot induction bends produced from high strength Q&T seamless pipes, it is more difficult to develop the required grade, combined with good impact toughness and low surface hardness values, while developing concurrently good HIC and SSC resistance. This problem is mainly related to the process conditions used during heat treatment of bends which are necessarily different from those of the seamless pipe. In particular, the quenching process of bends is less effective. This problem cannot be simply solved using steels with higher hardenability (i.e. higher content of chemical elements), because weldability is decreased, toughness is negatively affected, and the risk of hardness peaks is increased.

Examples of manufacturing processes and related steel pipes are disclosed in WO2013/002418, EP1918395A1, US2012/267014A1, US2013/000790A1 and EP1627931A1, the entirety of each is hereby incorporated by reference in their entirety.

WO2013/002418 discloses quenching and tempering conditions adjusted to have yield strength higher than 450 MPa and Vickers hardness HV₅ (load of 5 kgf=49 N), measured on the outer and inner side of a pipe, equal or lower than 250 HV₅ by carrying out a surface decarburization during heating before quenching and/or a mechanical grinding operation of the as-quenched pipe in order to decrease the surface hardness at the target values. The surface decarburization depth is of 2.5-3.0 mm, while the surface layer mechanically removed is of 0.3-0.7 mm.

EP1918395A1 discloses low carbon steels and a process of manufacturing seamless steel pipes in which, immediately after hot forming the seamless pipe, the pipe is quenched and tempered, or it is put into a holding furnace and soaked at a temperature not lower than Ac3 point, and then quenched and tempered. Therefore the process of EP1918395A1 performs an in-line treatment immediately after hot forming operations, while the pipe is still at temperatures above Ar3 (i.e. without occurring phase transformation from austenite to ferrite). Tempering includes reheating below Ac1 followed by air cooling. Such a process, carried out by using the disclosed low carbon steels, produces grain size numbers defined in the Japanese standard JIS G0551 (1998) that correspond to values of prior austenite grain size (mean lineal intercept, ASTM E112) higher than 32 μm. Disadvantageously these high values of prior austenite grain size (AGS), for these low carbon steels, mean higher steel hardenability with consequently very high hardness values obtained after quenching, whereby, also after tempering, maximum hardness values below 250 HV₁₀ at 1.5-2.0 mm depth from pipe surface cannot be assured. Moreover, coarse AGS leads to poor toughness as impact energy and shear area values are negatively affected by coarse grain population.

US2013/000790A1 discloses that the steel pipe is subjected, immediately after hot rolling and before quenching and tempering, to an optional reheating step S4 (FIG. 5) and/or to an accelerated water cooling step S5 with a cooling rate of at least 100° C./min and a cooling stop temperature of 550° to 450° C. in order to avoid precipitation of carbo-nitrides. After this accelerated-interrupted cooling the pipes have very poor grain growth inhibition. Therefore, coarse austenite grain size (AGS), higher than 25 μm, is expected in these pipes, that means higher steel hardenability with consequently maximum hardness values of 250 HV₁₀ or greater at 1.5 mm depth from pipe surface. Therefore, also poor SSC resistance is expected for these materials close to pipe surfaces.

US2012/267014A1 discloses a process for manufacturing a seamless steel pipe for linepipe capable of improving toughness. The pipe is subjected, after hot rolling and before austenitizing, quenching, and tempering, to an optional reheating step S4 (FIG. 4) and/or to an accelerated water cooling step with a cooling rate of at least 10° C./s. This accelerated water cooling of the hot rolled pipe is stopped when the surface temperature of the pipe reaches at most 450° C. The water cooling stop temperature is preferably at least 300° C., further preferably at least 350° C., and still further preferably at least 400° C., thus the room temperature is not reached. Disadvantageously coarse austenite grain size (AGS), higher than 25 μm, is expected in these pipes. Moreover, the pipes produced with this process are not suitable for severe linepipe applications where resistance to very sour environments and weldability are required.

At last, EP1627931A1 discloses a seamless pipe with a steel composition without Ca and having both V and Nb as mandatory elements, with a (V+Nb) content higher than 0.07%. Disadvantageously this high content of V and Nb contributes to the tempering resistance of bainite and martensite by precipitation hardening, increasing the difficulty in maintaining the maximum hardness below or equal to 235 HV₁₀, close to the outer and inner surfaces of the pipe. Moreover, the control of the shape of inclusions and the enhancement of the HIC resistance by forming fine and substantially round sulfides is not guaranteed due to Ca absence.

Therefore new solutions, which are outside of the conventional pattern for (micro)-alloying additions followed so far for Q&T seamless pipes and hot induction bends, have to be found for high performance X60Q, X65Q and X70Q grade medium wall seamless pipes, with maximum hardness lower than or equal to 235 HV₁₀ and very good impact toughness at low temperature (≦−60° C.).

SUMMARY

It is an object of certain embodiments of the present disclosure to make a medium wall quenched and tempered seamless steel pipe which offers a combination of consistently low maximum hardness values also close to external and internal pipe surfaces, excellent low temperature toughness and corrosion resistance (sour service, H2S environment), and good weldability.

It is a further object of certain embodiments of the present disclosure to provide a manufacturing process of the aforesaid seamless steel pipe.

Some embodiments of the present disclosure propose to reach the aforesaid objects by making a seamless quenched and tempered steel pipe which has a yield strength from 415 MPa to 635 MPa and a wall thickness (WT) higher than or equal to 6 mm and lower than or equal to 35 mm, wherein the steel pipe has a chemical composition comprising or consisting of 0.050-0.090 wt % C, 0.80-1.65 wt % Mn, 0.10-0.45 wt % Si, 0.10-0.60 wt % Cr, 0.05-0.45 wt % Ni, 0.05-0.40 wt % Mo, 0.020-0.040 wt % Al, 0.0030-0.0090 wt % N, 0.0008-0.0050 wt % Ca, 0.000-0.040 wt % Nb, 0.000-0.020 wt % Ti, 0.000-0.070 wt % V, 0.000-0.030 wt % Zr, 0.000-0.030 wt % Ta, 0.00-0.25 wt % Cu, 0.000-0.003 wt % S, 0.000-0.018 wt % P, 0.0000-0.0005 wt % B, and Fe (for example, the balance being iron), wherein at least one of Nb and V is present, (V+Nb) content being lower than 0.07 wt %, wherein, defining a first parameter P1=(60×C)+Cr+[5×e(35×Mo/WT)]+50×(V+Nb), the chemical composition satisfies a first condition 10≦P1≦14.5, wherein the quenched and tempered steel pipe has, at mid thickness and possibly also at the inner surface of the pipe, a microstructure comprising or consisting of, in volume percentage, tempered bainite greater than or equal to 40% and ferrite (VF) lower than or equal to 60%, and has at a distance up to 2 mm, starting from both outer and inner surfaces of the pipe or possibly from the outer surface only, a microstructure comprising or consisting of, in volume percentage, tempered martensite lower than 70%, tempered bainite higher than 30% and traces of ferrite less than or equal to 10%, wherein the microstructure of the quenched and tempered steel pipe has an average prior austenite grain size, measured by ASTM Standard E112, smaller than 25 μm, and wherein the maximum hardness values, measured at 1.5-2.0 mm depth from the outer and inner surfaces, are not higher than 235 HV10.

Certain embodiments of the present disclosure relate to a manufacturing process of the aforesaid seamless steel pipe in which there are provided the following steps:

-   -   a) hot forming a seamless steel pipe having a chemical         composition as described above and a wall thickness WT higher         than or equal to 6 mm and lower than or equal to 35 mm;     -   b) cooling the seamless steel pipe in air up to reach room         temperature;     -   c) heating the seamless steel pipe, with a first heating rate         between 0.1° C./s and 10° C./s, to an austenitizing temperature         above the Ac3 transformation point, in a range between 880° C.         and 980° C., and providing a soaking time between 180 s and 5400         s;     -   d) quenching the seamless steel pipe with a cooling rate in the         range of 20 to 80° C./s at mid thickness of the pipe, or at mid         thickness and at the inner surface of the pipe, and with a         cooling rate of 100-200° C./s in proximity of the outer and         inner surfaces of the pipe or in proximity of the outer surface         only;     -   e) heating the seamless steel pipe, with a second heating rate         between 0.1° C./s and 10° C./s, to a tempering temperature         comprised in a predetermined range, and providing a holding time         at said tempering temperature between 600 s and 7200 s,         wherein said predetermined range is calculated with a tolerance         of ±20° C. using the following equation:

$\begin{matrix} {{T\left( {{^\circ}\mspace{14mu}{C.}} \right)} = {\frac{1000 \times \left( {0.82 + C + {4.5 \times {Cr}} + {11.5 \times {Mo}} + {25 \times V}} \right)}{a - {3.8 \times C} + {4.3 \times {Cr}} + {10.6 \times {Mo}} + {22 \times V}} - 273.15}} & \left( {{eq}.\mspace{14mu} 3} \right) \end{matrix}$ where a is a parameter whose value is 1.75, 1.90 or 2.15 if the grade to be achieved is the X60, X65 or X70, respectively.

The seamless quenched and tempered (Q&T) steel pipes of certain embodiments of the disclosure are suitable for line pipes, flowlines and risers of grades X60Q, X65Q and X70Q, and preferably have an outside diameter (OD) between 3½″ (89 mm) and 28″ (711 mm).

After the manufacture of the medium wall seamless pipes, in certain embodiments, the same can be subjected to bending operations and heat treatments to obtain bends of grades X60Q, X65Q and X70Q with low maximum hardness and improved toughness at low temperature. Said bends have a yield strength from 415 to 635 MPa; maximum hardness values, measured at 1.5-2.0 mm depth from the surface, below 235 HV10 or equal to 235HV10; good impact toughness at low temperature (minimum impact energy of 150 J for transverse CVN tests performed on standard size specimens at −40° C.), while concurrently possessing good Hydrogen induced cracking (HIC) and sulfide stress corrosion cracking (SSC) resistance.

Defining the parameter P1=(60×C)+Cr+[5×e(35×Mo/WT)]+50×(V+Nb), the steel pipe of certain embodiments of the disclosure can meet the requirements of low maximum hardness (in particular at the part of wall thickness proximal to the outside and inside surfaces of the pipe), specified minimum yield strength (SMYS), toughness and corrosion resistance by satisfying the following condition: P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]+50×(V+Nb)≦14.5, preferably P1≦13.5,

-   -   where the symbols for the chemical elements represent the value         of the weight percentage (wt %) and WT is the wall thickness         value in mm.

Moreover, defining the parameter P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V), some embodiments of the disclosure can obtain an adequate hardenability to guarantee the minimum specified tensile properties at mid thickness if the parameter P2 satisfies the conditions summarized the following table:

grade WT < 20 mm 20 ≦ WT ≦ 35 mm X60 ≧2.00 ≧2.20 X65 ≧2.10 ≧2.30 X70 ≧2.35 ≧2.45 where in the parameter P2 the symbols for the chemical elements represent the value of the weight percentage (wt %).

Some embodiments of steel pipes manufactured according to the present disclosure can exhibit:

-   -   Yield strength, YS: 415 MPa (60.2 ksi) minimum and 635 MPa (92.1         ksi) maximum.     -   Ultimate Tensile Strength, UTS: 520 MPa (75.4 ksi) minimum and         760 MPa (110.2 ksi) maximum.     -   Elongation, not less than 18%.     -   YS/UTS ratio not higher than 0.90.         -   Maximum hardness (measured at 1.5 mm to 2.0 mm depth from             the pipe surface) not higher than 235 HV₁₀, preferably not             higher than 230 HV₁₀, and more preferably not higher than             225 HV₁₀.         -   Minimum impact energy of 200 J/150 J (average/individual)             and minimum 85% of average shear area for both longitudinal             and transverse Charpy V-notch (CVN) tests performed on             standard size specimens at −40° C. according with standard             ASTM A 370.     -   Ductile-Brittle Transformation Temperature (ASTM E23) less than         or equal to about −60° C.     -   hydrogen induced cracking (HIC) resistance, assessed according         with NACE Standard TM0284-2003 Item No. 21215, using NACE         solution A and test duration 96 hours, with the following HIC         parameters (average on three sections of three specimens):         -   Crack Length Ratio, CLR≦10%         -   Crack Thickness Ratio, CTR≦3%         -   Crack Sensitivity Ratio, CSR≦0.5%.     -   sulfide stress corrosion (SSC) cracking resistance, assessed in         accordance with ASTM G39, using NACE TM0177 test solution A and         a duration of 720 hours, with no failure at 90% of the actual         yield stress (AYS).

All these characteristics were achieved through a tailored metallurgical design of pipes by means of laboratory tests and industrial trials. The results show that the manufacture of Q&T seamless pipes and bends with maximum hardness not higher than 235 HV10, preferably not higher than 230 HV10, and more preferably not higher than 225 HV10, is possible at least within a determined dimensional range: outside diameter (OD) varying from 3½″ (89 mm) to 28″ (711 mm), and wall thickness (WT) from 6 mm to 35 mm.

In particular, the steel pipes of certain embodiments of the present disclosure have maximum hardness, measured at 1.5-2.0 mm depth from the internal and external surfaces, not higher than 235 HV10 for the grade X70Q, not higher than 230 HV10 for the grade X65Q, and not higher than 225 HV10 for the grade X60Q.

In one embodiment, a seamless quenched and tempered steel pipe comprises a yield strength from 415 MPa to 635 MPa and a wall thickness WT higher than or equal to 6 mm and lower than 35 mm, wherein the steel pipe has a chemical composition comprising:

Fe;

0.050-0.090 wt % C;

0.80-1.65 wt % Mn;

0.10-0.45 wt % Si;

0.10-0.60 wt % Cr;

0.05-0.45 wt % Ni;

0.05-0.40 wt % Mo;

0.020-0.040 wt % Al;

0.0030-0.0090 wt % N;

0.0008-0.0050 wt % Ca;

0.000-0.040 wt % Nb;

0.000-0.020 wt % Ti;

0.000-0.070 wt % V;

0.000-0.030 wt % Zr;

0.000-0.030 wt % Ta;

0.00-0.25 wt % Cu;

0.000-0.003 wt % S;

0.000-0.018 wt % P;

0.0000-0.0005 wt % B based on the composition weight;

wherein at least one of Nb and V is present, (V+Nb) content being lower than 0.07 wt %;

wherein, defining a first parameter: P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]50×(V+Nb),

the chemical composition satisfies a first condition 10≦P1≦14.5;

wherein the quenched and tempered steel pipe has, at mid thickness and possibly also at the inner surface of the pipe, a microstructure comprising, in volume percentage, tempered bainite greater than or equal to 40% and ferrite (V_(F)) lower than or equal to 60%;

and has at a distance up to 2 mm, starting from both outer and inner surfaces of the pipe or possibly from the outer surface only, a microstructure comprising, in volume percentage, tempered martensite lower than 70%, tempered bainite higher than 30% and traces of ferrite less than or equal to 10%;

wherein the microstructure of the quenched and tempered steel pipe has an average prior austenite grain size, measured by ASTM Standard E112, smaller than 25 μm;

and wherein the maximum hardness values, measured at 1.5-2.0 mm depth from the outer and inner surfaces, are not higher than 235 HV₁₀.

In some embodiments, the chemical composition can define a second parameter P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V), the chemical composition can satisfy a second condition P2≧2.00.

In some embodiments, the second condition, as a function of grade and wall thickness (WT), can be:

grade WT < 20 mm 20 ≦ WT ≦ 35 mm X60 P2 ≧ 2.00 P2 ≧ 2.20 X65 P2 ≧ 2.10 P2 ≧ 2.30 X70 P2 ≧ 2.35 P2 ≧ 2.45

In some embodiments, at a distance up to 2 mm starting from outer surface or from both outer and inner surfaces of the steel pipe, the microstructure can comprise of tempered martensite lower than 40% and tempered bainite higher than 60%. In some embodiments, at a distance up to 2 mm starting from outer surface or from both outer and inner surfaces of the steel pipe, the microstructure can comprise tempered martensite lower than 20% and tempered bainite higher than 80%. In some embodiments, at mid thickness, the microstructure can comprise tempered bainite greater than or equal to 50% and ferrite (V_(F)) lower than or equal to 50%. In some embodiments, at mid thickness, the microstructure can comprise tempered bainite greater than or equal to 80% and ferrite (V_(F)) lower than or equal to 20%.

In some embodiments, the (V+Nb) content can be lower than 0.055 wt %.

In some embodiments, at mid thickness and possibly also at the inner surface of the pipe, the microstructure can comprise ferrite (V_(F)) lower than or equal to 60% for a pipe of grade X60, ferrite (V_(F)) lower than or equal to 40% for a pipe of grade X65, ferrite (V_(F)) lower than or equal to 20% for a pipe of grade X70.8.

In some embodiments, CE_(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15) can be in the range of 0.26% to 0.43%, and CE_(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B can be in the range of 0.14% to 0.22%.

In some embodiments, the chemical composition can comprise:

Fe;

0.050-0.090 wt % C;

0.90-1.35 wt % Mn;

0.10-0.35 wt % Si;

0.10-0.40 wt % Cr;

0.05-0.40 wt % Ni;

0.07-0.40 wt % Mo;

0-0.070 wt % V;

0.020-0.040 wt % Al;

0.0008-0.0030 wt % Ca;

0.000-0.035 wt % Nb;

0.000-0.015 wt % Ti;

0.0030-0.0070 wt % N;

0.00-0.20 wt % Cu;

0.000-0.002 wt % S;

0.000-0.015 wt % P;

0.0000-0.0005 wt % B;

0.000-0.015 wt % Zr;

0.000-0.015 wt % Ta.

In some embodiments, the chemical composition can comprise:

Fe;

0.060-0.085 wt % C;

1.00-1.30 wt % Mn;

0.10-0.30 wt % Si;

0.20-0.40 wt % Cr;

0.20-0.40 wt % Ni;

0.10-0.35 wt % Mo;

0.000-0.070 wt % V;

0.020-0.040 wt % Al;

0.0015-0.0030 wt % Ca;

0.000-0.030 wt % Nb;

0.000-0.015 wt % Ti;

0.0030-0.0070 wt % N;

0.00-0.15 wt % Cu;

0.000-0.0015 wt % S;

0.000-0.012 wt % P;

0.0000-0.0005 wt % B;

0.000-0.010 wt % Zr;

0.000-0.010 wt % Ta.

In some embodiments, chemical composition can comprise:

Fe;

0.060-0.085 wt % C;

1.00-1.25 wt % Mn;

0.10-0.30 wt % Si;

0.30-0.40 wt % Cr;

0.25-0.35 wt % Ni;

0.25-0.35 wt % Mo;

0.000-0.040 wt % V;

0.020-0.035 wt % Al;

0.0010-0.0030 wt % Ca;

0.020-0.030 wt % Nb;

0.000-0.015 wt % Ti;

0.0030-0.0060 wt % N;

0.00-0.15 wt % Cu;

0.000-0.0015 wt % S;

0.000-0.011 wt % P;

0.0000-0.0005 wt % B;

0.000-0.010 wt % Zr;

0.000-0.010 wt % Ta.

In some embodiments, the chemical composition can comprise:

Fe;

0.050-0.090 wt % C;

0.90-1.30 wt % Mn;

0.10-0.35 wt % Si;

0.10-0.25 wt % Cr;

0.08-0.30 wt % Ni;

0.08-0.15 wt % Mo;

0.000-0.045 wt % V;

0.020-0.040 wt % Al;

0.0008-0.0030 wt % Ca;

0.000-0.035 wt % Nb;

0.000-0.015 wt % Ti;

0.0030-0.0070 wt % N;

0.00-0.20 wt % Cu;

0.000-0.002 wt % S;

0.000-0.015 wt % P;

0.0000-0.0001 wt % B;

0.000-0.010 wt % Zr;

0.000-0.010 wt % Ta;

and can satisfy the following additional conditions: CE _(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range 0.26% to 0.37%; CE _(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.14% to 0.18%; P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]+50×(V+Nb) in the range of 10 to 14.5; P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)≧2.0.

In some embodiments, the chemical composition can comprise:

Fe;

0.060-0.090 wt % C;

0.95-1.30 wt % Mn;

0.10-0.35 wt % Si;

0.10-0.30 wt % Cr;

0.20-0.40 wt % Ni;

0.14-0.25 wt % Mo;

0.000-0.045 wt % V;

0.020-0.040 wt % Al;

0.0008-0.0030 wt % Ca;

0.000-0.035 wt % Nb;

0.000-0.015 wt % Ti;

0.0030-0.0070 wt % N;

0.00-0.20 wt % Cu;

0.000-0.002 wt % S;

0.000-0.015 wt % P;

0.0000-0.0001 wt % B;

0.000-0.010 wt % Zr;

0.000-0.010 wt % Ta;

and can satisfy the following additional conditions: CE _(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range 0.36% to 0.43%; CE _(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.18% to 0.21%; P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]+50×(V+Nb) in the range of 10 to 14.5; P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)≧2.30.

In some embodiments, the chemical composition can comprise:

Fe;

0.060-0.090 wt % C;

0.95-1.30 wt % Mn;

0.10-0.35 wt % Si;

0.20-0.40 wt % Cr;

0.25-0.40 wt % Ni;

0.25-0.35 wt % Mo;

0.000-0.010 wt % V;

0.020-0.040 wt % Al;

0.0008-0.0030 wt % Ca;

0.020-0.035 wt % Nb;

0.000-0.015 wt % Ti;

0.0030-0.0070 wt % N;

0.00-0.20 wt % Cu;

0.000-0.002 wt % S;

0.000-0.015 wt % P;

0.0000-0.0001 wt % B;

0.000-0.010 wt % Zr;

0.000-0.010 wt % Ta;

and can satisfy the following additional conditions: CE _(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range 0.37% to 0.43%; CE _(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.18% to 0.21%; P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]+50×(V+Nb) in the range of 12 to 14.5; P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)≧2.30.

In some embodiments, the chemical composition can comprise:

Fe;

0.060-0.090 wt % C;

0.90-1.20 wt % Mn;

0.10-0.35 wt % Si;

0.10-0.25 wt % Cr;

0.05-0.20 wt % Ni;

0.05-0.15 wt % Mo;

0.000-0.070 wt % V;

0.020-0.040 wt % Al;

0.0008-0.0030 wt % Ca;

0.000-0.005 wt % Nb;

0.005-0.015 wt % Ti;

0.0030-0.0090 wt % N;

0.00-0.20 wt % Cu;

0.000-0.003 wt % S;

0.000-0.015 wt % P;

0.0000-0.0001 wt % B;

0.000-0.010 wt % Zr;

0.000-0.010 wt % Ta;

and can satisfy the following additional conditions: CE _(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range 0.26% to 0.36%; CE _(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.14% to 0.18%; P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]+50×(V+Nb) in the range of 10 to 14.5; P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)≧2.00.

In some embodiments, the chemical composition can comprise:

Fe;

0.060-0.090 wt % C;

0.95-1.30 wt % Mn;

0.10-0.35 wt % Si;

0.10-0.40 wt % Cr;

0.05-0.40 wt % Ni;

0.07-0.25 wt % Mo;

0.000-0.070 wt % V;

0.020-0.040 wt % Al;

0.0008-0.0030 wt % Ca;

0.000-0.005 wt % Nb;

0.005-0.015 wt % Ti;

0.0030-0.0080 wt % N;

0.00-0.20 wt % Cu;

0.000-0.003 wt % S;

0.000-0.015 wt % P;

0.0000-0.0001 wt % B;

0.000-0.010 wt % Zr;

0.000-0.010 wt % Ta;

and can satisfy the following additional conditions: CE _(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15) in the range 0.31% to 0.41%; CE _(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.15% to 0.20%; P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]+50×(V+Nb) in the range of 11 to 14.5; P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)≧2.30.

In some embodiments, the chemical composition can comprise:

Fe;

0.060-0.090 wt % C;

1.00-1.30 wt % Mn;

0.10-0.35 wt % Si;

0.20-0.40 wt % Cr;

0.20-0.40 wt % Ni;

0.10-0.25 wt % Mo;

0.000-0.070 wt % V;

0.020-0.040 wt % Al;

0.0008-0.0030 wt % Ca;

0.000-0.005 wt % Nb;

0.005-0.015 wt % Ti;

0.0030-0.0070 wt % N;

0.00-0.15 wt % Cu;

0.000-0.003 wt % S;

0.000-0.012 wt % P;

0.0000-0.0001 wt % B;

0.000-0.010 wt % Zr, 0.000-0.010 wt % Ta;

and can satisfy the following additional conditions: CE _(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range 0.37% to 0.43%; CE _(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.16% to 0.22%; P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]+50×(V+Nb) in the range of 12.5 to 14.5; P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)≧2.30.

Also disclosed herein are embodiments of a method of manufacturing a seamless quenched and tempered steel pipe which can comprise hot forming a seamless steel pipe having a wall thickness WT higher than or equal to 6 mm and lower than 35 mm and a chemical composition comprising:

Fe;

0.050-0.090 wt % C;

0.80-1.65 wt % Mn;

0.10-0.45 wt % Si;

0.10-0.60 wt % Cr;

0.05-0.45 wt % Ni;

0.05-0.40 wt % Mo;

0.020-0.040 wt % Al;

0.0030-0.0090 wt % N;

0.0008-0.0050 wt % Ca;

0.000-0.040 wt % Nb;

0.000-0.020 wt % Ti;

0.000-0.070 wt % V;

0.000-0.030 wt % Zr;

0.000-0.030 wt % Ta;

0.00-0.25 wt % Cu;

0.000-0.003 wt % S;

0.000-0.018 wt % P;

0.0000-0.0005 wt % B;

cooling the seamless steel pipe in air up to reach the room temperature;

heating the seamless steel pipe, with a first heating rate between 0.1° C./s and 10° C./s, to an austenitizing temperature above the Ac3 transformation point, in a range between 880° C. and 980° C., and providing a soaking time between 180 s and 5400 s;

quenching the seamless steel pipe with a cooling rate in the range of 20 to 80° C./s at mid thickness of the pipe, or at mid thickness and at the inner surface of the pipe, and with a cooling rate of 100-200° C./s in proximity of the outer and inner surfaces of the pipe or in proximity of the outer surface only;

heating the seamless steel pipe, with a second heating rate between 0.1° C./s and 10° C./s, to a tempering temperature comprised in a predetermined range, and providing a holding time at said tempering temperature between 600 s and 7200 s,

wherein said predetermined range is calculated with a tolerance of ±20° C. using the following equation:

${T\left( {{^\circ}\mspace{14mu}{C.}} \right)} = {\frac{1000 \times \left( {0.82 + C + {4.5 \times {Cr}} + {11.5 \times {Mo}} + {22 \times V}} \right)}{a - {3.8 \times C} + {4.3 \times {Cr}} + {10.6 \times {Mo}} + {22 \times V}} - 273.15}$

where a is a parameter whose value is 1.75, 1.90 or 2.15 if the grade to be achieved is the X60, X65 or X70, respectively; and wherein the final steel pipe has a yield strength from 415 MPa to 635 MPa.

In some embodiments, the heating step can occur in gas-fired furnace, provided with at least one burner, in which the oxygen concentration can be less than 10%, preferably in the range of 0.5% to 4%.

In some embodiments, at the exit from the gas-fired furnace the pipe can be immediately descaled by high pressure water and moved in less than 120 s in a water quenching system.

Also disclosed is a pipe bend, which can be obtainable by an above steel pipe composition, and can have maximum hardness values, measured at 1.5 mm to 2 mm depth from the surface, not higher than 235 HV₁₀,

In some embodiments, the pipe bend can have maximum hardness values, measured at 1.5 mm to 2 mm depth from the surface, not higher than 230 HV₁₀.

With respect to the above described compositions or as described elsewhere in this specification, where compositions are described as “comprising” certain elements,” the chemical composition may alternatively “consist of” or “consist essentially of” the listed elements. If the chemical composition “consists of” or “consists essentially of” certain elements, the chemical composition can have a balance of Fe with or without inevitable impurities.

Following is an illustrative listing of some additional embodiments within the scope of this disclosure. These embodiments are examples only and are not intended to be limiting. Although there may be some embodiments within the scope of this disclosure that are not expressly recited below or elsewhere herein, the present disclosure contemplates and includes all embodiments within the scope of what this disclosure shows and describes. Further, this disclosure contemplates and includes embodiments comprising any combination of any structure, material, step, or other feature disclosed anywhere herein with any other structure, material, step, or other feature disclosed anywhere herein.

Embodiment 1

A seamless quenched and tempered steel pipe having a yield strength from 415 MPa to 635 MPa and a wall thickness WT higher than or equal to 6 mm and lower than 35 mm, wherein the steel pipe has a chemical composition consisting of 0.050-0.090 wt % C, 0.80-1.65 wt % Mn, 0.10-0.45 wt % Si, 0.10-0.60 wt % Cr, 0.05-0.45 wt % Ni, 0.05-0.40 wt % Mo, 0.020-0.040 wt % Al, 0.0030-0.0090 wt % N, 0.0008-0.0050 wt % Ca, 0.000-0.040 wt % Nb, 0.000-0.020 wt % Ti, 0.000-0.070 wt % V, 0.000-0.030 wt % Zr, 0.000-0.030 wt % Ta, 0.00-0.25 wt % Cu, 0.000-0.003 wt % S, 0.000-0.018 wt % P, 0.0000-0.0005 wt % B based on the composition weight, the remaining being iron; wherein at least one of Nb and V is present, (V+Nb) content being lower than 0.07 wt %; wherein, defining a first parameter P1=(60×C)+Cr+[5×e^((35×Mo/WT))]+50×(V+Nb), the chemical composition satisfies a first condition 10≦P1≦14.5; wherein the quenched and tempered steel pipe has, at mid thickness and possibly also at the inner surface of the pipe, a microstructure consisting of, in volume percentage, tempered bainite greater than or equal to 40% and ferrite (V_(F)) lower than or equal to 60%, and has at a distance up to 2 mm, starting from both outer and inner surfaces of the pipe or possibly from the outer surface only, a microstructure consisting of, in volume percentage, tempered martensite lower than 70%, tempered bainite higher than 30% and traces of ferrite less than or equal to 10%, wherein the microstructure of the quenched and tempered steel pipe has an average prior austenite grain size, measured by ASTM Standard E112, smaller than 25 μm, and wherein the maximum hardness values, measured at 1.5-2.0 mm depth from the outer and inner surfaces, are not higher than 235 HV₁₀.

Embodiment 2

The seamless quenched and tempered steel pipe according to embodiment 1, wherein, defining a second parameter P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V), the chemical composition satisfies a second condition P2≧2.00.

Embodiment 3

The seamless quenched and tempered steel pipe according to embodiment 2, wherein the second condition, as a function of grade and wall thickness (WT), is:

grade WT < 20 mm 20 ≦ WT ≦ 35 mm X60 P2 ≧ 2.00 P2 ≧ 2.20 X65 P2 ≧ 2.10 P2 ≧ 2.30 X70 P2 ≧ 2.35 P2 ≧ 2.45

Embodiment 4

The seamless quenched and tempered steel pipe according to any of the preceding embodiments, wherein, at a distance up to 2 mm starting from outer surface or from both outer and inner surfaces of the steel pipe, the microstructure consists of tempered martensite lower than 40% and tempered bainite higher than 60%, preferably tempered martensite lower than 20% and tempered bainite higher than 80%.

Embodiment 5

The seamless quenched and tempered steel pipe according to any one of the preceding embodiments, wherein, at mid thickness, the microstructure consists of tempered bainite greater than or equal to 50% and ferrite (V_(F)) lower than or equal to 50%, preferably tempered bainite greater than or equal to 80% and ferrite (V_(F)) lower than or equal to 20%.

Embodiment 6

The seamless quenched and tempered steel pipe according to any one of the preceding embodiments, wherein the (V+Nb) content is lower than 0.055 wt %.

Embodiment 7

The seamless quenched and tempered steel pipe according to embodiment 1, wherein, at mid thickness and possibly also at the inner surface of the pipe, the microstructure comprises ferrite (V_(F)) lower than or equal to 60% for a pipe of grade X60, ferrite (V_(F)) lower than or equal to 40% for a pipe of grade X65, ferrite (V_(F)) lower than or equal to 20% for a pipe of grade X70.8. Seamless quenched and tempered steel pipe according to any one of the preceding claims, wherein CE_(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15) is in the range of 0.26% to 0.43%, and CE_(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B is in the range of 0.14% to 0.22%.

Embodiment 9

The seamless quenched and tempered steel pipe according to any one of the preceding embodiments, wherein the chemical composition consists of: 0.050-0.090 wt % C, 0.90-1.35 wt % Mn, 0.10-0.35 wt % Si, 0.10-0.40 wt % Cr, 0.05-0.40 wt % Ni, 0.07-0.40 wt % Mo, 0-0.070 wt % V, 0.020-0.040 wt % Al, 0.0008-0.0030 wt % Ca, 0.000-0.035 wt % Nb, 0.000-0.015 wt % Ti, 0.0030-0.0070 wt % N, 0.00-0.20 wt % Cu, 0.000-0.002 wt % S, 0.000-0.015 wt % P, 0.0000-0.0005 wt % B, 0.000-0.015 wt % Zr, 0.000-0.015 wt % Ta, the remaining being iron.

Embodiment 10

The seamless quenched and tempered steel pipe according to embodiment 9, wherein the chemical composition consists of: 0.060-0.085 wt % C, 1.00-1.30 wt % Mn, 0.10-0.30 wt % Si, 0.20-0.40 wt % Cr, 0.20-0.40 wt % Ni, 0.10-0.35 wt % Mo, 0.000-0.070 wt % V, 0.020-0.040 wt % Al, 0.0015-0.0030 wt % Ca, 0.000-0.030 wt % Nb, 0.000-0.015 wt % Ti, 0.0030-0.0070 wt % N, 0.00-0.15 wt % Cu, 0.000-0.0015 wt % S, 0.000-0.012 wt % P, 0.0000-0.0005 wt % B, 0.000-0.010 wt % Zr, 0.000-0.010 wt % Ta, the remaining being iron.

Embodiment 11

The seamless quenched and tempered steel pipe according to embodiment 10, wherein the chemical composition consists of: 0.060-0.085 wt % C, 1.00-1.25 wt % Mn, 0.10-0.30 wt % Si, 0.30-0.40 wt % Cr, 0.25-0.35 wt % Ni, 0.25-0.35 wt % Mo, 0.000-0.040 wt % V, 0.020-0.035 wt % Al, 0.0010-0.0030 wt % Ca, 0.020-0.030 wt % Nb, 0.000-0.015 wt % Ti, 0.0030-0.0060 wt % N, 0.00-0.15 wt % Cu, 0.000-0.0015 wt % S, 0.000-0.011 wt % P, 0.0000-0.0005 wt % B, 0.000-0.010 wt % Zr, 0.000-0.010 wt % Ta, the remaining being iron.

Embodiment 12

The seamless quenched and tempered steel pipe according to any one of embodiments 1 to 8, wherein the chemical composition consists of 0.050-0.090 wt % C, 0.90-1.30 wt % Mn, 0.10-0.35 wt % Si, 0.10-0.25 wt % Cr, 0.08-0.30 wt % Ni, 0.08-0.15 wt % Mo, 0.000-0.045 wt % V, 0.020-0.040 wt % Al, 0.0008-0.0030 wt % Ca, 0.000-0.035 wt % Nb, 0.000-0.015 wt % Ti, 0.0030-0.0070 wt % N, 0.00-0.20 wt % Cu, 0.000-0.002 wt % S, 0.000-0.015 wt % P, 0.0000-0.0001 wt % B, 0.000-0.010 wt % Zr, 0.000-0.010 wt % Ta, the remaining being iron; and satisfies the following additional conditions: CE_(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range 0.26% to 0.37%; CE_(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.14% to 0.18%; P1=(60×C)+Cr+[5×e^((35×Mo/WT))]+50×(V+Nb) in the range of 10 to 14.5; P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)≧2.0.

Embodiment 13

The seamless quenched and tempered steel pipe according to any one of embodiments 1 to 8, wherein the chemical composition consists of 0.060-0.090 wt % C, 0.95-1.30 wt % Mn, 0.10-0.35 wt % Si, 0.10-0.30 wt % Cr, 0.20-0.40 wt % Ni, 0.14-0.25 wt % Mo, 0.000-0.045 wt % V, 0.020-0.040 wt % Al, 0.0008-0.0030 wt % Ca, 0.000-0.035 wt % Nb, 0.000-0.015 wt % Ti, 0.0030-0.0070 wt % N, 0.00-0.20 wt % Cu, 0.000-0.002 wt % S, 0.000-0.015 wt % P, 0.0000-0.0001 wt % B, 0.000-0.010 wt % Zr, 0.000-0.010 wt % Ta, the remaining being iron; and satisfies the following additional conditions: CE_(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range 0.36% to 0.43%; CE_(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.18% to 0.21%; P1=(60×C)+Cr+[5×e^((35×Mo/WT))]+50×(V+Nb) in the range of 10 to 14.5; P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×)≧2.30.

Embodiment 14

The seamless quenched and tempered steel pipe according to any one of embodiments 1 to 8, wherein the chemical composition consists of 0.060-0.090 wt % C, 0.95-1.30 wt % Mn, 0.10-0.35 wt % Si, 0.20-0.40 wt % Cr, 0.25-0.40 wt % Ni, 0.25-0.35 wt % Mo, 0.000-0.010 wt % V, 0.020-0.040 wt % Al, 0.0008-0.0030 wt % Ca, 0.020-0.035 wt % Nb, 0.000-0.015 wt % Ti, 0.0030-0.0070 wt % N, 0.00-0.20 wt % Cu, 0.000-0.002 wt % S, 0.000-0.015 wt % P, 0.0000-0.0001 wt % B, 0.000-0.010 wt % Zr, 0.000-0.010 wt % Ta, the remaining being iron; and satisfies the following additional conditions: CE_(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range 0.37% to 0.43%; CE_(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.18% to 0.21%; P1=(60×C)+Cr+[5×e^((35×Mo/WT))]+50×(V+Nb) in the range of 12 to 14.5; P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)≧2.30.

Embodiment 15

The seamless quenched and tempered steel pipe according to any one of embodiments 1 to 8, wherein the chemical composition consists of 0.060-0.090 wt % C, 0.90-1.20 wt % Mn, 0.10-0.35 wt % Si, 0.10-0.25 wt % Cr, 0.05-0.20 wt % Ni, 0.05-0.15 wt % Mo, 0.000-0.070 wt % V, 0.020-0.040 wt % Al, 0.0008-0.0030 wt % Ca, 0.000-0.005 wt % Nb, 0.005-0.015 wt % Ti, 0.0030-0.0090 wt % N, 0.00-0.20 wt % Cu, 0.000-0.003 wt % S, 0.000-0.015 wt % P, 0.0000-0.0001 wt % B, 0.000-0.010 wt % Zr, 0.000-0.010 wt % Ta, the remaining being iron; and satisfies the following additional conditions: CE_(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range 0.26% to 0.36%; CE_(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.14% to 0.18%; P1=(60×C)+Cr+[5×e^((35×Mo/WT))]+50×(V+Nb) in the range of 10 to 14.5; P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)≧2.00.

Embodiment 16

The seamless quenched and tempered steel pipe according to any one of embodiments 1 to 8, wherein the chemical composition consists of 0.060-0.090 wt % C, 0.95-1.30 wt % Mn, 0.10-0.35 wt % Si, 0.10-0.40 wt % Cr, 0.05-0.40 wt % Ni, 0.07-0.25 wt % Mo, 0.000-0.070 wt % V, 0.020-0.040 wt % Al, 0.0008-0.0030 wt % Ca, 0.000-0.005 wt % Nb, 0.005-0.015 wt % Ti, 0.0030-0.0080 wt % N, 0.00-0.20 wt % Cu, 0.000-0.003 wt % S, 0.000-0.015 wt % P, 0.0000-0.0001 wt % B, 0.000-0.010 wt % Zr, 0.000-0.010 wt % Ta, the remaining being iron; and satisfies the following additional conditions: CE_(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15) in the range 0.31% to 0.41%; CE_(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.15% to 0.20%; P1=(60×C)+Cr+[5×e^((35×Mo/WT))]+50×(V+Nb) in the range of 11 to 14.5; P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)≧2.30.

Embodiment 17

The seamless quenched and tempered steel pipe according to any one of embodiments 1 to 8, wherein the chemical composition consists of 0.060-0.090 wt % C, 1.00-1.30 wt % Mn, 0.10-0.35 wt % Si, 0.20-0.40 wt % Cr, 0.20-0.40 wt % Ni, 0.10-0.25 wt % Mo, 0.000-0.070 wt % V, 0.020-0.040 wt % Al, 0.0008-0.0030 wt % Ca, 0.000-0.005 wt % Nb, 0.005-0.015 wt % Ti, 0.0030-0.0070 wt % N, 0.00-0.15 wt % Cu, 0.000-0.003 wt % S, 0.000-0.012 wt % P, 0.0000-0.0001 wt % B, 0.000-0.010 wt % Zr, 0.000-0.010 wt % Ta, the remaining being iron; and satisfies the following additional conditions: CE_(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range 0.37% to 0.43%; CE_(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.16% to 0.22%; P1=(60×C)+Cr+[5×e^((35×Mo/WT))]+50×(V+Nb) in the range of 12.5 to 14.5; P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)≧2.30.

Embodiment 18

A process of manufacturing a seamless quenched and tempered steel pipe having a yield strength from 415 MPa to 635 MPa, the process consisting of the following steps:

-   -   a) hot forming a seamless steel pipe having a chemical         composition according to claim 1 and a wall thickness WT higher         than or equal to 6 mm and lower than 35 mm;     -   b) cooling the seamless steel pipe in air up to reach the room         temperature;     -   c) heating the seamless steel pipe, with a first heating rate         between 0.1° C./s and 10° C./s, to an austenitizing temperature         above the Ac3 transformation point, in a range between 880° C.         and 980° C., and providing a soaking time between 180 s and 5400         s;     -   d) quenching the seamless steel pipe with a cooling rate in the         range of 20 to 80° C./s at mid thickness of the pipe, or at mid         thickness and at the inner surface of the pipe, and with a         cooling rate of 100-200° C./s in proximity of the outer and         inner surfaces of the pipe or in proximity of the outer surface         only;     -   e) heating the seamless steel pipe, with a second heating rate         between 0.1° C./s and 10° C./s, to a tempering temperature         comprised in a predetermined range, and providing a holding time         at said tempering temperature between 600 s and 7200 s,     -   wherein said predetermined range is calculated with a tolerance         of ±20° C. using the following equation:

$\begin{matrix} {{T\left( {{^\circ}\mspace{14mu}{C.}} \right)} = {\frac{1000 \times \left( {0.82 + C + {4.5 \times {Cr}} + {11.5 \times {Mo}} + {25 \times V}} \right)}{a - {3.8 \times C} + {4.3 \times {Cr}} + {10.6 \times {Mo}} + {22 \times V}} - 273.15}} & \left( {{eq}.\mspace{14mu} 3} \right) \end{matrix}$

-   -   where a is a parameter whose value is 1.75, 1.90 or 2.15 if the         grade to be achieved is the X60, X65 or X70, respectively.

Embodiment 19

The process according to embodiment 18, wherein the heating of the step c) occurs in gas-fired furnace, provided with at least one burner, in which the oxygen concentration is less than 10%, preferably in the range of 0.5% to 4%.

Embodiment 20

The process according to embodiment 19, wherein at the exit from the gas-fired furnace the pipe is immediately descaled by high pressure water and moved in less than 120 s in a water quenching system.

Embodiment 21

A bend, obtainable by a seamless steel pipe according to embodiment 1, having maximum hardness values, measured at 1.5 mm to 2 mm depth from the surface, not higher than 235 HV₁₀, preferably not higher than 230 HV₁₀.

BRIEF DESCRIPTION OF THE DRAWINGS

Further features and advantages of embodiments of the present disclosure may be more apparent in the light of the detailed description of seamless steel pipes and of a manufacturing process thereof, illustrated by way of non-limitative example, with the aid of the accompanying drawing.

The FIGURE is an embodiment of a flow diagram of the process according to the disclosure.

DETAILED DESCRIPTION

The seamless steel pipe, subject of certain embodiments of the present disclosure, can be designed in order to have not only the medium hardness value along the whole wall thickness but also the maximum hardness values below or equal to 235 HV₁₀, preferably below or equal to 230 HV₁₀, and more preferably not higher than 225 HV₁₀, also in proximity of both internal and external surfaces of the pipe, combined with good toughness at low temperatures, resistance to sulfide stress corrosion cracking (SSC) and hydrogen induced cracking (HIC), which can enable use of the pipe in sour service environments. Said maximum hardness values have been measured at 1.5 mm to 2.0 mm depth from both the internal and external surfaces of the pipes, according to ISO 3183, hereby incorporated by reference in its entirety.

The term “pipe”, as used herein, refers to a hollow, elongate member which can be straight or have bends or curves and be formed to a predetermined shape, and any additional forming required to secure the formed tubular product in its intended location. The pipe can have a substantially cylindrical outer surface and inner surface, although other shapes and cross-sections are contemplated as well.

The term “room temperature” as used herein has its ordinary meaning as known to those skilled in the art and may include temperatures within the range of about 16° C. (60° F.) to about 32° C. (90° F.).

Regarding the steel composition, the term “optional element” refers to an element that is possibly added to the chemical composition of embodiment of the steel pipes of the disclosure. Each optional element can be added to further improve the properties of the steel pipes. For example, optional elements in the steel of the seamless pipes of certain embodiments of the disclosure are: vanadium (V), niobium (Nb), titanium (Ti), zirconium (Zr), tantalum (Ta).

In particular, vanadium and niobium are optional elements that, if present, must satisfy the condition (V+Nb)<0.07%. In some preferred embodiments at least one of V and Nb is present and the (V+Nb) content is lower than 0.07%, preferably lower than or equal to 0.055%. In seamless steel pipes of the prior art higher contents of vanadium and niobium caused maximum hardness values higher than 235HV10, in particular in proximity of the pipe surfaces, even if the medium or average hardness value along the whole wall thickness was lower than 235HV10. The term “medium or average hardness” means the average value of the hardness values measured along the wall thickness of the pipe.

The term “impurity element”, instead, refers to an element not provided in the design of the steel composition. However, said element may be present as impurity or traces because, depending on the manufacturing process, its presence may be unavoidable. In order to optimize the properties of embodiments of the steel pipes of the disclosure, the content of each impurity element has been appropriately limited. Said impurity elements can be: copper (Cu), sulfur (S), phosphorous (P), boron (B).

The maximum value of all impurities in the steel composition is advantageously lower than or equal to 0.30 wt %, preferably equal to about 0.27 wt %.

The seamless steel pipes according to certain embodiments of the disclosure can be employed, for example, as linepipes, flowlines and risers for use in the oil and gas industry. Said pipes can have a wall thickness greater than or equal to 6 mm and less than or equal to 35 mm and, globally, a predominant microstructure of bainite, as explained later in greater detail. Said pipes can possess a minimum yield strength of at least 415 MPa (60 ksi), covering the mechanical properties corresponding to different grades: X60Q (minimum yield strength of 415 MPa=60.2 ksi), X65Q (minimum yield strength of 450 MPa=65 ksi), and X70Q (minimum yield strength of 485 MPa=70 ksi).

As discussed in detail below, through a combination of steel composition and heat treatment, a final microstructure of certain embodiments can be achieved that gives rise to selected mechanical properties of interest in medium wall seamless pipes.

The steel composition of some embodiments of the present disclosure can comprise low carbon (C), manganese (Mn), silicon (Si), chromium (Cr), nickel (Ni), molybdenum (Mo), nitrogen (N), aluminum (Al) and calcium (Ca). Additionally, one or more of the following elements can be optionally added: niobium (Nb), vanadium (V), titanium (Ti), zirconium (Zr), tantalum (Ta). The remainder of the composition can comprise iron (Fe) and possible impurities. The concentration of said impurities can be reduced to as low an amount as possible. Said impurities can include copper (Cu), sulfur (S), phosphorous (P), boron (B).

Hardenability of the steel, i.e. the relative ability of the steel to form bainite and martensite when quenched, has been improved through the chemical composition in certain embodiments. In particular, addition of elements such as Mo, Mn, Cr, and Ni in the ranges below described can be effective in promoting predominantly bainite formation instead of ferrite.

As the process of cleavage fracture initiation is considered as composed of three stages: (I) formation of fracture origin by cementite cracking, (II) propagation of the crack in cementite into the matrix and formation of a cleavage crack, and (III) propagation of the cleavage crack across high angle grain boundaries, both a low number per unit volume of cementite particles and a high frequency of high angle boundaries (fine packets) lead to a better impact toughness at low-temperature.

Low C content can avoid the formation of an excessive number of coarse cementite particles, but can reduce hardenability and can increase transformation temperatures. Therefore, C decrease can be combined with proper Mn, Cr, Ni, and Mo additions to reduce transformation temperatures and maintain fine the packet size.

In some embodiments, steels were identified as having:

limitation of vanadium content plus niobium content (V+Nb) to values lower than 0.07%, preferably lower than 0.055%,

and carbon content from 0.050 to 0.090%, where the lower the carbon content in the steel the higher the level of other alloying elements such as Mn, Mo, Cr, and Ni.

Advantageously the combination of the chemical elements can be optimized in order to maintain low the maximum hardness value and induce good weldability, maintaining the carbon equivalent CE_(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range from 0.26% to 0.43%. Moreover, preferably, the carbon equivalent CE_(Pcm) values (CE_(Pcm)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B) are in the range from 0.14 to 0.22. The symbols of the chemical elements for the carbon equivalents Ce_(IIW) and CE_(Pcm) represent the value of the respective weight percentage (wt %).

Advantageously the requirements of appropriately reduced maximum hardness values (along the whole thickness of the pipe), of minimum strength, toughness and corrosion resistance can be consistently guaranteed if the parameter P1 defined by the equation 1: P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]+50×(V+Nb)  (eq. 1) and can satisfy the condition P1≦14.5, preferably P1≦13.5.

Advantageously P1 can be higher than or equal to 10.0.

The steel pipes of certain embodiments of the disclosure can have a U-shaped hardness profile along the wall thickness, with the highest values at the inner and outer surfaces and the lowest values at mid-thickness. Adequate hardenability to guarantee the minimum specified tensile properties at mid thickness can be achieved if the parameter P2 defined by equation 2, P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)  (eq. 2) satisfies the minimum values summarized in the following table, as a function of grade and wall thickness:

grade WT < 20 mm 20 ≦ WT ≦ 35 mm X60 ≧2.00 ≧2.20 X65 ≧2.10 ≧2.30 X70 ≧2.35 ≧2.45

The symbol “x” in the equations 1, 2 and in the formula of the carbon equivalent CEPcm is a multiplication sign. In the equations 1 and 2 and in the formula both of CEPcm and CeIIW the symbols for the chemical elements represent the value of the weight percentage (wt %).

Table 1 illustrates some embodiments of the steel composition, in weight percent (wt. %):

TABLE 1 Steel composition ranges (weight percent wt %) PREFERRED CHEMICAL COMPOSITIONS Composition 1 Composition 2 Composition 3 Composition 4 Element P/O/I (*) Min. Max. Min. Max. Min. Max. Min. Max. C P 0.050 0.090 0.050 0.090 0.060 0.085 0.060 0.085 Mn P 0.80 1.65 0.90 1.35 1.00 1.30 1.00 1.25 Si P 0.10 0.45 0.10 0.35 0.10 0.30 0.10 0.30 Cr P 0.10 0.60 0.10 0.40 0.20 0.40 0.30 0.40 Ni P 0.05 0.45 0.05 0.40 0.20 0.40 0.25 0.35 Mo P 0.05 0.40 0.07 0.40 0.10 0.35 0.25 0.35 Nb O 0.000 0.040 0.000 0.035 0.000 0.030 0.020 0.030 Ti O 0.000 0.020 0.000 0.015 0.000 0.015 0.000 0.015 V O 0.000 0.070 0.000 0.070 0.000 0.070 0.000 0.040 Al P 0.020 0.040 0.020 0.040 0.020 0.040 0.020 0.035 N P 0.0030 0.0090 0.0030 0.0070 0.0030 0.0070 0.0030 0.0060 Cu I 0.00 0.25 0.00 0.20 0.00 0.15 0.00 0.15 S I 0.000 0.003 0.000 0.002 0.000 0.0015 0.000 0.0015 P I 0.000 0.018 0.000 0.015 0.000 0.012 0.000 0.011 Ca P 0.0008 0.0050 0.0008 0.0030 0.0015 0.0030 0.0010 0.0030 B I 0.0000 0.0005 0.0000 0.0005 0.0000 0.0005 0.0000 0.0005 Zr O 0.000 0.030 0.000 0.015 0.000 0.010 0.000 0.010 Ta O 0.000 0.030 0.000 0.015 0.000 0.010 0.000 0.010 Nb + V — 0.00 <0.07 0.00 <0.07 0.00 <0.07 0.00 <0.07 (*) P = Present; O = Optional; I = Impurity

Some embodiments (Composition 5) of the steel composition can have the same ranges of the Composition 3, except for the maximum value of Nb that is equal to 0.005 wt %.

Carbon (C) is an element whose addition to the steel composition can inexpensively raise the strength of the steel and refine the microstructure, reducing the transformation temperatures. If the C content of the steel composition is less than about 0.050%, it can be difficult to obtain the strength desired in the pipes. On the other hand, if the steel composition has a C content greater than about 0.090%, maximum hardness can be above 235 HV₁₀, toughness can be impaired, and weldability can decrease, making more difficult and expensive any welding process. Therefore, the C content of the steel composition can be selected within the range of 0.050% to 0.090%, and preferably within the range of 0.060% to 0.085%.

Manganese (Mn) is an element whose addition to the steel composition can be effective in increasing the hardenability, strength and toughness of the steel. If the Mn content of the steel composition is less than about 0.80% it can be difficult to obtain the desired strength in the steel. However, if the Mn content of the steel composition exceeds 1.65% banding structures become marked, and toughness and HIC/SSC resistance decrease. Therefore, the Mn content of the steel composition can be selected within the range of 0.80% to 1.65%, preferably within the range of 0.90% to 1.35%, and more preferably within the range of 1.00% to 1.30%. In a preferred embodiment Mn content can be greater than or equal to 1.00% and less than or equal to 1.25%.

Silicon (Si) is an element whose addition to the steel composition can have a deoxidizing effect during steel making process and can also raise the strength of the steel (e.g., solid solution strengthening). If the Si content of the steel composition is less than 0.10%, the steel can be poorly deoxidized during steelmaking process and can exhibit a high level of micro-inclusions. If the Si content of the steel composition exceeds 0.45%, both toughness and formability of the steel can decrease. Si content higher than about 0.45% can be also recognized to have a detrimental effect on surface quality when the steel is processed at high temperatures (e.g., temperatures greater than about 1000° C.) in oxidizing atmospheres, because surface oxide (scale) adherence can be increased due to fayalite formation and the risk of surface defect is higher. Therefore, the Si content of the steel composition can be selected within the range between 0.10% to 0.45%, preferably within the range of 0.10% to 0.35%, and more preferably within the range of 0.10% to 0.30%.

Chromium (Cr) is an element whose addition to the steel composition can increase hardenability, decrease transformation temperatures, and increase tempering resistance of the steel. Therefore the addition of Cr to steel composition can be desirable for achieving high strength and toughness levels. If the Cr content of the steel composition is less than 0.10% it can be difficult to obtain the desired strength and toughness. On the other hand, if the Cr content of the steel composition exceeds about 0.60%, the cost can be excessive and toughness decreases due to enhanced precipitation of coarse carbides at grain boundaries. In addition, weldability of the resultant steel can be reduced, making the welding process more difficult and expensive. Therefore the Cr content of the steel composition can be selected within the range of 0.10% to 0.60%, preferably within the range of 0.10% to 0.40%, and more preferably within the range of 0.20% to 0.40%. In a preferred embodiment Cr content can be greater than or equal to 0.30% and less than or equal to 0.40%.

Nickel (Ni) is an element whose addition can increase the strength and toughness of the steel. However, when Ni addition exceeds 0.45%, a more adherent scale has been observed, with higher risk of surface defect formation. Moreover, Ni contents higher than 1% are recognized to have a detrimental effect on sulfide stress corrosion (SSC) cracking. Instead, if Ni content is lower than 0.05% the effect on toughness and strength can become negligible.

Therefore, the Ni content of certain embodiments of the steel composition can vary within the range of 0.05% to 0.45%, preferably within the range of 0.05% to 0.40%, and more preferably within the range of 0.20% to 0.40%. In a preferred embodiment Ni content can be greater than or equal to 0.25% and less than or equal to 0.35%.

Molybdenum (Mo) is an element whose addition to the steel composition can improve hardenability and hardening by solid solution and fine precipitation. Mo assists in retarding softening during tempering, promoting the formation of very fine MC and M₂C precipitates. These particles can be substantially uniformly distributed in the matrix and also act as beneficial hydrogen traps, slowing down the atomic hydrogen diffusion towards the dangerous traps, usually at grain boundaries, which behave as crack nucleation sites. Mo also can reduce the segregation of phosphorous to grain boundaries, improving resistance to intergranular fracture, with beneficial effects also on SSC resistance because high strength steels which suffer hydrogen embrittlement exhibit an intergranular fracture morphology. By increasing the Mo content, the desired strength can be achieved at higher tempering temperatures, which promote better toughness levels. In order to exert the effect thereof, the Mo content of the steel composition can be greater than or equal to 0.05%. However, for Mo contents higher than 0.40% weldability can be reduced. As Mo ferroalloy is expensive, the Mo content can be selected within the range of 0.05% to 0.40%, preferably within the range of 0.07% to 0.40%, and more preferably within the range of 0.10% to 0.35%. In a preferred embodiment Mo content can be greater than or equal to 0.25% and less than or equal to 0.35%.

Niobium (Nb) is an optional element whose addition to the steel composition can be used to refine further the austenitic grain size during hot rolling and re-heating before quenching, as it can hinder the movement of grain boundaries acting both in solid solution and in the form of fine carbides and nitrides.

Nb can increase the steel strength by particle dispersion hardening and can contribute to generate high hardness values in bainite and martensite after tempering. These fine and round particles can be substantially uniformly distributed in the matrix and also act as hydrogen traps, beneficially slowing down the atomic hydrogen diffusion towards the dangerous traps, usually at grain boundaries, which behave as crack nucleation sites. If the Nb content is higher than 0.040%, a coarse precipitate distribution that impair toughness is formed. Moreover, if the Nb content is higher than 0.040%, it can promote the formation of brittle zones in the heat affected zone (HAZ) of the girth weld. Therefore, the Nb content of the steel composition can be selected to be less than or equal to about 0.040% (0.000% possibly included), preferably less than or equal to 0.035%, and more preferably less than or equal to 0.030%. In a preferred embodiment Nb content can be greater than or equal to 0.020% and less than or equal to 0.030%. In a further preferred embodiment Nb content can be less than or equal to 0.005% (0.000% possibly included).

Vanadium (V) is an optional element whose addition to the steel composition can increase strength by very fine carbonitride precipitation during tempering. However, if a significant volume fraction of vanadium carbide particles is formed, difficulties in maintaining high toughness levels and maximum hardness values lower than or equal to 235 HV₁₀ can be experienced after tempering. Therefore, the V content of the steel composition can be maintained to be less than or equal to 0.070% (0.000% possibly included). In a preferred embodiment V content can be less than or equal to 0.040%, preferably less than or equal to 0.030%.

Both vanadium and niobium can contribute to the tempering resistance of bainite and martensite by precipitation hardening, increasing the difficulty in maintaining the maximum hardness below or equal to the value of 235 HV₁₀, in particular close to the outer and inner surfaces of the pipe where the presence of significant amounts of martensite cannot be excluded. Therefore the sum of vanadium and niobium content of the steel composition can be less than 0.07%, preferably lower than or equal to 0.055%. Advantageously at least one of vanadium and niobium can be present.

Titanium (Ti) is an optional element whose addition to the steel composition can be provided to refine austenitic grain size in high temperature processes, forming nitrides and carbonitrides. When Ti is present in concentrations higher than 0.020%, coarse TiN particles can be formed that impair toughness. Accordingly, the Ti content of the steel composition can be less than or equal to 0.020% (0.000% possibly included), preferably less than or equal to 0.015%. In some embodiments of the steel titanium (Ti) can be an element with its content selected to be greater than or equal to 0.006% and less than or equal to 0.020%, preferably greater than or equal to 0.006% and less than or equal to 0.015%.

Aluminum (Al) is an element whose addition to the steel composition can have a deoxidizing effect during steel making process and may refine the steel grain. Therefore, Al content can be equal to or greater than 0.020%. If the Al content of the steel composition is higher than about 0.040%, coarse precipitates of AlN that impair toughness and/or Al-rich oxides (e.g., non-metallic inclusions) that impair HIC and SSC resistance may be formed. Accordingly the Al content of the steel can be selected to be in the range of 0.020% to 0.040%, preferably in the range of 0.020% to 0.035%. In a preferred embodiment Al content can be greater than or equal to 0.020% and less than or equal to 0.035%.

Nitrogen (N) is an element whose presence within the steel composition can contribute to form carbonitrides of Nb, Mo and Ti and help to achieve the minimum strength. However if the N content of the steel composition exceeds 0.0090%, the toughness of the steel may be degraded. Moreover, when nitrogen content is above said limit value, the response to strain-aging can be impaired due to the increase of yield to tensile ratio and ductile-brittle transition temperature. Therefore, the N content of the steel composition can be selected in the range of 0.0030% to 0.0090%, preferably within the range of 0.0030% to 0.0070%. In a preferred embodiment N content can be greater than or equal to 0.0030% and less than or equal to 0.0060%.

Copper (Cu) can be an impurity element that is not needed in the embodiments of the steel composition. However, depending on the manufacturing process, the presence of Cu may be unavoidable. Therefore, the Cu content can be limited to as low as possible in order to maintain the risk of hot cracking (hot shortness) and defect formation induced by adherent scale at very low levels. For example the Cu content of the steel composition can be less than or equal to 0.25% (0.00% possibly included), preferably less than or equal to 0.20%, and more preferably less than or equal to 0.15%. Among the possible impurities copper is the element that can be present with higher wt % and its possible presence is due to the manufacturing process. These maximum limits are typical of a steel production route based on Electrical Arc Furnace (EAF) and use of scrap. Intensive recycling is now a common practice over the world for the production of long/tubular and flat products, and this recycling can determine the presence of copper as an impurity at the above mentioned levels.

Sulfur (S) can be an impurity element that may decrease both toughness and workability of the steel, as well as HIC/SSC resistance. Accordingly, the S content of the steel can be kept as low as possible. For example the S content of the steel composition can be less than or equal to 0.0030% (0.0000% possibly included), preferably less than or equal to 0.0020%, and more preferably less than or equal to 0.0015%.

Phosphorous (P) can be an impurity element that may cause the toughness and HIC/SSC resistance of high strength steel to decrease. Accordingly, the P content can be kept as low as possible. For example the P content of the steel composition may be less than or equal to about 0.018% (0.000% possibly included), preferably less than or equal to about 0.015%, more preferably less than or equal to about 0.012%. In a preferred embodiment P content is less than or equal to 0.011%.

Calcium (Ca) is an element whose addition to the steel composition can assist with control of the shape of inclusions and enhancement of the HIC resistance by forming fine and substantially round sulfides. In order to provide these benefits, the Ca content of the steel composition can be selected to be greater than or equal to about 0.0008%. However, if the Ca content of the steel composition exceeds 0.0050% the effect of the Ca addition can be saturated and the risk of forming clusters of Ca-rich non-metallic inclusions that reduce HIC and SSC resistance is increased. Accordingly, the Ca content of the steel composition can be selected to be within the range of 0.0008% to 0.0050%, preferably within the range of 0.0008% to 0.0030%. In a preferred embodiment Ca content can be greater than or equal to 0.0015% and less than or equal to 0.0030%. In a further preferred embodiment Ca content can be greater than or equal to 0.0010% and less than or equal to 0.0030%.

Boron (B) can be an impurity element whose presence in the steel composition can be undesired as it increases steel hardenability and hardness in the HAZ. The upper limit of B content to avoid these detrimental effects is about 0.0005%. Therefore, the maximum B content of the steel composition can be selected to be less than or equal to 0.0005% (0.0000% possibly included).

Zirconium (Zr) and tantalum (Ta) are optional elements that can act as strong carbide and nitride formers, similar to Nb and Ti. These elements can be optionally added to the steel composition of certain embodiments in order to produce Zr and Ta fine carbonitrides that can increase the steel strength by particle dispersion hardening and also can act as beneficial hydrogen traps, slowing down the atomic hydrogen diffusion towards the dangerous traps. If the Zr or Ta content is greater than or equal to 0.030%, a coarse precipitate distribution that may impair toughness of the steel can be formed. Zirconium also can act as a deoxidizing element in the steel and combines with sulphur; however, as addition to steel in order to promote globular non-metallic inclusions, Ca may be preferred. Therefore, the content of Zr or Ta within the steel composition can be selected to be less than or equal to 0.030% (0.000% possibly included), preferably less than or equal to 0.015%, and more preferably less than or equal to 0.010%.

A process for manufacturing some embodiments of the seamless steel pipes is schematically illustrated in the flow diagram of the FIGURE. The process can include steelmaking operations 102; hot forming operations 104; heat treatment operations 106, which can include austenitizing 106A, quenching 106B and tempering 106C; and finishing operations 110. Steelmaking operations to prepare the steel compositions of Table 1 and hot forming operations to produce a seamless steel pipe having a wall thickness in the range of 6 to 35 mm can include known methodologies.

In some embodiments, steelmaking operations 102 can comprise fabrication of the steel and production of a solid metal billet capable of being pierced and rolled to form a metallic tubular product. Selected steel scrap, cast iron, and sponge iron may be employed to prepare the raw material for the steel composition. Other sources of iron and/or steel may be employed for preparation of the steel composition.

Primary steelmaking may be performed using an electric arc furnace to melt the steel, decrease phosphorous and other impurities, and achieve a selected temperature in certain embodiments. Tapping and deoxidation, and addition of alloying elements may be further performed.

In some embodiments, the steelmaking process can refine the iron by removal of impurities. In particular, sulfur and phosphorous can be prejudicial for steel because they degrade the mechanical properties of the steel and resistance to HIC and SSC. In some embodiments, secondary steelmaking may be performed in a ladle furnace and trimming station after primary steelmaking to perform specific purification steps.

During these operations, in some embodiments very low sulfur contents can be achieved within the steel, calcium inclusion treatment is performed, and inclusion flotation is performed. Inclusion flotation may be performed by bubbling inert gases in the ladle furnace to force inclusions and impurities to float. This technique produces a fluid slag capable of absorbing impurities and inclusions. In this manner, high quality steel having the desired composition with low inclusion content can be provided.

Following the production of the melt steel having a composition within the ranges of Table 1, in certain embodiments steel is cast as a round solid billet having a substantially uniform diameter along the longitudinal axis thereof. For example, round billets having a diameter within the range between about 190 mm to about 420 mm may be produced in this manner.

The billet thus fabricated can be formed into a tubular product through hot forming processes 104 in some embodiments. A solid, cylindrical billet of clean steel may be heated to a temperature of about 1200° C. to 1340° C., preferably about 1280° C. For example, the billet may be reheated by a rotary hearth furnace. The billet can be further subject to a hot piercing and rolling operation. Within the rolling mill the billet can be pierced, for example using the Mannessmann effect, and a hot deformation process can be used to substantially reduce the outside diameter and wall thickness of the pipe, while the length is substantially increased. The piercing process may be performed at temperatures within the range between about 1200° C. to about 1300° C.

In certain embodiments, the obtained hollow bars can be subjected to hot rolling at temperatures within the range between about 1000° C. and about 1200° C. in a retained mandrel continuous mill or similar/equivalent mill.

Accurate sizing may be then carried out by a sizing mill.

The seamless pipes are, after hot forming and before austenitizing, quenching and tempering, directly cooled in air, preferably still air, to about room temperature in a cooling bed in some embodiments. The air-cooled pipes can have a microstructure of ferrite and pearlite, due to the relatively slow cooling rate during cooling in still air between 800° C. and 500° C., said slow cooling rate being in the range of about 0.5-2° C./s, depending on thickness. Moreover, the air-cooled pipes already can contain fine precipitates (e.g. Nb and/or V carbo-nitrides) formed during air-cooling, which can be very effective in inhibiting austenite grain growth during reheating (austenitizing) before quenching. For example, pipes with outer diameters (OD) within the range between about 3½ inches to about 16 inches may be formed in this manner.

In some embodiments, after hot rolling the pipes may be in-line heated, without cooling at room temperature, by an intermediate furnace for making temperature more uniform, and accurate sizing may be carried out by a sizing mill. Subsequently, the seamless pipes can be immediately cooled in air, preferably still air, down to room temperature in a cooling bed.

In the case of a pipe having a final OD greater than about 16 inches, the pipes produced by a medium size mill may be processed by a rotary expansion mill in certain embodiments. For example, medium size pipes may be reheated by a walking beam furnace to a temperature within the range between about 1150° C. to about 1250° C., expanded to the desired diameter by the expander mill at a temperature within the range between about 1100° C. to about 1200° C., and in-line reheated before final sizing.

In a non-limiting example, a solid bar may be hot formed as discussed above into a pipe possessing an outer diameter within the range of about 3½ inches to about 28 inches and a wall thickness greater than or equal to 6 mm and less than or equal to 35 mm.

The final microstructure of the formed pipe can be determined by the composition of the steel provided in steelmaking operations 102 and heat treatments performed in operations 106. The composition and microstructure, in turn, can give rise to the properties of the formed pipe.

The heat treatment operations 106, carried out after having cooled the pipe in air to about room temperature, can include austenitizing, quenching and tempering (Q+T) in some embodiments.

Therefore the process of some embodiments of the disclosure can carry out an off-line quenching (or reheating quenching) which can involve cooling the pipe down to room temperature, then heating the pipe until phase transformation to austenite has fully occurred, and finally quenching and tempering (reheating below Act, austenite start transformation point, followed by air cooling).

This off-line quenching in some embodiments, through austenite-ferrite-austenite transformation, can promote the refinement of the austenite grains and make them more uniform, when compared with the microstructure of in-line quenched material.

A consequence of this process is that the average prior austenite grain size (AGS), measured as mean lineal intercept by ASTM Standard E112, can be ≦25 μm, corresponding to a prior austenite grain size number higher than or equal to 7.3 according to the Japanese standard JIS G0551 or the same ASTM Standard E112, each hereby incorporated by reference in their entirety, allowing to achieve a better toughness.

The austenitizing operation can include reheating the pipe from about room temperature (reached after hot forming by means of the cooling in air) to a temperature that austenitizes the pipe followed by a rapid quench in certain embodiments.

In some embodiments, a heating of the seamless steel pipe can be carried out, with a heating rate between 0.1° C./s and 10° C./s, to an austenitizing temperature above the Ac3 transformation point, in a range between 880° C. and 980° C., and providing a soaking time between 180 s and 5400 s.

This heating of the austenitizing operation can be carried out in a gas-fired furnace provided with burners. The heat source during re-heating for austenitizing can be due to combustion of natural gas (CH₄). Therefore oxygen can be consumed during combustion, but advantageously oxygen concentration in the furnace can be less than 10%. Typically oxygen content can be in the range of 0.5% to 4% and decarburizing process can be very limited, with typical decarburizing depths of 0.05 mm to 0.15 mm (maximum value).

For example, the temperatures of the austenitizing furnace may be selected in order to allow the pipe to achieve the target austenitizing temperature with a tolerance lower than about +/−30° C. in some embodiments. The austenitizing temperatures can be above the Ac3 transformation point, preferably in the range between 900° C. to 960° C., more preferably in the range between 910° C. and 930° C. The heating rate may be selected within the range between 0.1° C./s to 8° C./s. The soaking time, the time from when the pipe achieves the final target temperature minus 10° C. to the exit of the pipe from the furnace, may be selected within the range between 300 s to 3600 s. Austenitizing temperatures and soaking times may be selected depending on chemical composition, wall thickness, and desired austenite grain size. At the exit of the furnace, the pipe may be descaled, for example by high pressure water, to remove the surface oxide and is rapidly moved, preferably in less than 120 s, to a quenching system, for example a water quenching system.

In the quenching operations 106B, in some embodiments external and internal cooling can be employed to achieve at mid thickness the desired cooling rates, greater than about 20° C./s, preferably in the range between 20° C./s and 80° C./s. In some embodiments, said cooling rate can be in the range of 50° C./s to 80° C./s. Instead, in proximity of the outer and inner surfaces of the pipe, in particular at 1.5-2 mm depth from said surfaces, the cooling rate can be in the range between 100 and 200° C./s.

In some embodiments, in the quenching operations 106B, external cooling can be employed to achieve at mid thickness and also at the inner pipe surface the desired cooling rates, greater than about 20° C./s, preferably in the range between 20° C./s and 80° C./s. In some embodiments, said cooling rate can be in the range of 50° C./s to 80° C./s. Instead, in proximity of the outer surface of the pipe, in particular at 1.5-2 mm depth from said surfaces, the cooling rate can be in the range between 100 and 200° C./s. In the case of wall thickness lower than about 25 mm, an external quenching by means of water jets rings can be employed.

For example, a water quenching can be performed by dipping the pipe in a tank containing stirred water in some embodiments. The pipe can be rapidly rotated during quenching to make the heat transfer high and uniform and avoid pipe distortion. Additionally, in order to remove the steam developed inside the pipe, an inner water jet may also be employed. The water temperature may not be higher than about 40° C., preferably less than about 30° C. during quenching operations 106B.

Advantageously the pipe during immersion in the water tank can be under rotation and a water jet can be ejected by a nozzle inside the pipe in order to remove steam and avoid film formation. In this manner a uniform and effective quenching can be carried out because a film boiling state is avoided. In fact, in case of a film boiling state, the heat transfer is not so homogeneous along the pipe and lower cooling rates are obtained at mid-wall, with the risk that the desired yield strength may not be achieved.

In some embodiments, after said quenching operations 106B the seamless steel pipes, having a chemical composition according one of the embodiments of Table 1 and a wall thickness greater than or equal to 6 mm and less than or equal to 35 mm, promote, in the global microstructure of the steel pipe, the formation of a volume percent of bainite greater than 40%, preferably greater than 50% and more preferably greater than 80%, and lower than or equal to 90%.

In some embodiments, at mid thickness (and possibly also at the inner surface of the pipe) the microstructure of the quenched steel pipe can comprise in volume percentage bainite greater than or equal to 40% and ferrite (V_(F)), for example fine polygonal ferrite, lower than or equal to 60%, with smaller amounts of MA constituent (high-C martensite and retained austenite islands). In some embodiments, bainite can be greater than or equal to 50% and ferrite (V_(F)) is lower than or equal to 50%. In some embodiments, bainite can be greater than or equal to 80% and ferrite (V_(F)) is lower than or equal to 20%. MA constituent can be present in volume fractions up to approximately 12%.

Advantageously, at distances up to approximately 2 mm from outer and inner surfaces of the steel pipes (or possibly at distances up to approximately 2 mm from the outer surface only), the microstructure of the quenched steel pipe can be constituted of martensite with volume percentages lower than 70%, preferably lower than 40%, and most preferably lower than 20% (measured according with ASTM E562-08, hereby incorporated by reference in its entirety) and of bainite in a volume percentage higher than 30%, preferably higher than 60%, most preferably higher than 80%. Traces of ferrite, up to about 10%, may be present in the steels with lower hardenability. Martensite and bainite can be formed at temperatures lower than 450° C. and 600° C., respectively, after re-heating at austenitizing temperatures in the range of 900° C. to 960° C. for soaking times between 300 s to 3600 s, and quenching at cooling rates equal or greater than 20° C./s, preferably in the range of 20 to 80° C./s, at mid thickness in the case of external and internal quenching, or both at mid thickness and at the inner pipe surface in the case of only external quenching.

In addition, the average prior austenite grain size, measured by ASTM Standard E112, hereby incorporated by reference in its entirety, can be advantageously smaller than 25 μm (lineal intercept).

The average size of regions separated by high angle boundaries (i.e. the packet size) can be advantageously smaller than 9 μm, preferably smaller than 7 μm, most preferably smaller than 5 μm. Said packet size can be measured as average lineal intercept on images taken by Scanning Electron Microscopy (SEM) using the Electron Back Scattered Diffraction (EBSD) signal, and considering high-angle boundaries those with misorientation >15°.

After quenching operation 106B, in some embodiments the pipe can be introduced in another furnace for the tempering operations 106C, comprising a heating of the seamless steel pipe to a tempering temperature in a range between 600° C. and 680° C., and providing a holding time at said tempering temperature between 600 s and 7200 s.

The tolerances for the selected tempering temperature can be within the range of about ±15° C. The pipe can be heated at a rate between about 0.1° C./s to about 10° C./s to the selected tempering temperature. The pipe can be further held at the selected tempering temperature for a duration of time preferably within the range between 600 s and 5400 s.

In certain embodiments, the tempering temperature can be selected within the range between about 600° C. and about 680° C. depending on the chemical composition of the steel and the grade to be achieved.

Embodiments of an optimum tempering temperature range can be calculated with a tolerance of ±20° C., preferably ±10° C., using the following equation 3:

$\begin{matrix} {{T\left( {{^\circ}\mspace{14mu}{C.}} \right)} = {\frac{1000 \times \left( {0.82 + C + {4.5 \times {Cr}} + {11.5 \times {Mo}} + {25 \times V}} \right)}{a - {3.8 \times C} + {4.3 \times {Cr}} + {10.6 \times {Mo}} + {22 \times V}} - 273.15}} & \left( {{eq}.\mspace{14mu} 3} \right) \end{matrix}$ where a is a parameter having a value equal to 1.75, 1.90 or 2.15 if the grade to be achieved is the X60Q, X65Q or X70Q, respectively. The symbol “x” is a multiplication sign and the symbols for the chemical elements represent the value of the weight percentage.

For example, if the tempering temperature calculated by means of the equation 3 is equal to 647° C. (according the chemical composition of the example 2, see below, for a grade X60 steel pipe), the optimum tempering range is from 627° C. to 667° C., whereby the tempering temperature can be chosen within this optimum range.

In particular, at mid thickness (and possibly also at the inner surface of the pipe) the microstructure of the quenched and tempered steel pipe can comprise in volume percentage tempered bainite greater than or equal to 40% and ferrite (VF), for example fine polygonal ferrite, lower than or equal to 60%, while the MA constituent may be now absent because during tempering MA islands decompose in ferrite and carbides, such as a decomposition requiring temperatures higher than 550° C. and being necessary not to impair the toughness of the final product. Preferably tempered bainite can be greater than or equal to 50% and ferrite (VF) is lower than or equal to 50%. More preferably tempered bainite can be greater than or equal to 80% and ferrite (VF) is lower than or equal to 20%.

Advantageously, at distances up to approximately 2 mm from outer and inner surfaces of the steel pipes (or possibly at distances up to approximately 2 mm from the outer surface only), the microstructure of the quenched and tempered steel pipe can comprise tempered martensite with volume percentages lower than 70%, preferably lower than 40%, and most preferably lower than 20% (measured according with ASTM E562-08, hereby incorporated by reference in its entirety) and tempered bainite in a volume percentage higher than 30%, preferably higher than 60%, most preferably higher than 80%. Traces of ferrite, up to about 10%, may be present in the steels with lower hardenability.

After tempering, in some embodiments the microstructure can still have an average prior austenite grain size, measured by ASTM Standard E112, hereby incorporated by reference in its entirety, advantageously smaller than 25 μm (lineal intercept).

The average size of regions separated by high angle boundaries (i.e. the packet size) can be advantageously smaller than 9 μm, preferably smaller than 7 μm, most preferably smaller than 5 μm. By forming a microstructure including tempered bainite, as opposed to a banded microstructure (e.g., ferrite-pearlite), the HIC resistance of the steel pipe can be further increased. Said packet size can be measured as average lineal intercept on images taken by Scanning Electron Microscopy (SEM) using the Electron Back Scattered Diffraction (EBSD) signal, and considering high-angle boundaries those with misorientation >15°.

In some embodiments, the tempered microstructure may also include presence of fine precipitates of MX, M2X type (where M is Mo, Nb, or Cr and X is C or N) with size less than 40 nm, in addition to precipitates of the type M3C with an average diameter of about 80 nm to about 400 nm (measured by Transmission Electron Microscopy).

Finishing operations 110 may include, but are not limited to, straightening and hot bending operations in certain embodiments.

In some embodiments, straightening may be performed at temperatures below the tempering temperature and above about 450° C.

Bending of quenched and tempered seamless pipe may be performed by hot induction. Hot induction bending can be a hot deformation process which concentrates in a narrow zone, referred to as hot tape, that is defined by an induction coil (e.g., a heating ring) and a quenching ring that sprays water on the external surface of the structure to be bent. A straight (mother) pipe is pushed from its back, while the front of the pipe can be clamped to an arm constrained to describe a circular path. This constraint can provoke a bending moment on the entire structure, but the pipe can be plastically deformed substantially only within the zone corresponding to the hot tape. The quenching ring plays therefore two simultaneous roles: to define the zone under plastic deformation and to in-line quench the hot bend.

The diameter of both heating and quenching rings can be about 20 mm to about 60 mm larger than the outside diameter (OD) of the mother pipe in some embodiments. The bending temperature, for example in the range 800-870° C., at both exterior and interior surfaces of the pipe may be continuously measured by pyrometers. The bending rate can be preferably within the range 10-25 mm/min.

In conventional fabrication, the bends may be subjected to a stress relieving treatment after bending and quenching by a tempering treatment at a relatively low temperature to achieve the final mechanical properties.

However, it is recognized that the in-line quenching and tempering operations performed during finishing operations 110 may produce a microstructure that is different than that obtained from the off-line quenching and tempering operations 106B, 106C in certain embodiments. Therefore, as discussed above in operations 106B, 106C, in order to substantially regenerate the microstructure obtained after operations 106B and 106C, the bends can be advantageously subjected to off-line quenching and tempering in some embodiments. The bends can be reheated in a furnace at a rate within the range 0.05° C./s to approximately 1° C./s at a temperature between 900° C. and 960° C., and then rapidly immersed into a quenching tank with stirred water and then tempered in a furnace. The temper after bending can be performed at a temperature within the range between about 600° C. to about 680° C. The pipe can be heated at a rate within the range between about 0.05° C./s to approximately 1° C./s. A holding time within the range between about 600 s to about 5400 s may be employed after the target tempering temperature has been achieved.

The steel pipes of certain embodiments of the present disclosure, having a wall thickness higher than or equal to 6 mm and lower or equal to 35 mm, having a chemical composition according to Table 1, being subjected to the above mentioned manufacturing process including austenitizing, quenching and tempering operations, and having the above mentioned microstructure after tempering, can cover the grades X60Q and/or X65Q and/or X70Q.

A steel pipe of grade X65Q, having a WT greater than or equal to 6 mm and less than or equal to 35 mm and the composition and microstructure discussed above, can possess the following properties in some embodiments:

-   -   Yield strength, YS: 450 MPa (65.3 ksi) minimum and 600 MPa (87         ksi) maximum.     -   Ultimate Tensile Strength, UTS: 535 MPa (77.6 ksi) minimum and         760 MPa (110.2) maximum.     -   Elongation, not less than 20%, referred to a circular cross         section test piece of diameter 12.5 mm.     -   YS/UTS ratio not higher than 0.88.     -   Maximum hardness (measured at 1.5 mm depth from the pipe         surface) not higher than 230 HV₁₀, more preferably not higher         than 225 HV₁₀.     -   Minimum impact energy of 200 J/150 J (average/individual) and         minimum 85% of average shear area for both longitudinal and         transverse Charpy V-notch (CVN) tests performed on standard size         specimens or sub-size specimens when applicable at −40° C.         according with standard ISO 148-1.     -   Ductile-Brittle Transformation Temperature (ASTM E23) less than         or equal to about −60° C.     -   HIC resistance, assessed according with NACE Standard         TM0284-2003 Item No. 21215, using NACE solution A and test         duration 96 hours, with the following HIC parameters (average on         three sections of three specimens):         -   Crack Length Ratio, CLR≦10%         -   Crack Thickness Ratio, CTR≦3%         -   Crack Sensitivity Ratio, CSR≦0.5%     -   SSC resistance, assessed in accordance with ASTM G39, using NACE         TM0177 test solution A and a duration of 720 hours, with no         failure at 90% of the actual yield stress (AYS).

A steel pipe of grade X60Q, having a WT greater than or equal to 6 mm and less than or equal to 35 mm and the composition and microstructure discussed above, can possess the following properties in certain embodiments:

-   -   Yield strength, YS: 415 MPa (60.2 ksi) minimum and 565 MPa (81.9         ksi) maximum.     -   Ultimate Tensile Strength, UTS: 520 MPa (75.4 ksi) minimum and         760 MPa (110.2 ksi) maximum.     -   Elongation, not less than 20%, referred to a circular cross         section test piece of diameter 12.5 mm.     -   YS/UTS ratio not higher than 0.87.     -   Maximum hardness (measured at 1.5 mm to 2.0 mm depth from the         pipe surface) not higher than 225 HV₁₀.     -   Minimum impact energy of 200 J/150 J (average/individual) and         minimum 85% of average shear area for both longitudinal and         transverse Charpy V-notch (CVN) tests performed on standard size         specimens or sub-size specimens when applicable at −40° C.         according with standard ASTM A 370.     -   Ductile-Brittle Transformation Temperature (ASTM E23) less than         or equal to about −60° C.     -   HIC resistance, assessed according with NACE Standard         TM0284-2003 Item No. 21215, using NACE solution A and test         duration 96 hours, with the following HIC parameters (average on         three sections of three specimens):         -   Crack Length Ratio, CLR≦10%         -   Crack Thickness Ratio, CTR≦3%         -   Crack Sensitivity Ratio, CSR≦0.5%     -   SSC resistance, assessed in accordance with ASTM G39, using NACE         TM0177 test solution A and a duration of 720 hours, with no         failure at 90% of the actual yield stress (AYS).

A steel pipe of grade X70Q, having a WT greater than or equal to 6 mm and less than or equal to 35 mm and the composition and microstructure discussed above, can possess the following properties in some embodiments:

-   -   Yield strength, YS: 485 MPa (70.3 ksi) minimum and 635 MPa (92.1         ksi) maximum.     -   Ultimate Tensile Strength, UTS: 570 MPa (83 82.7 ksi) minimum         and 760 MPa (110.2 ksi) maximum.     -   Elongation, not less than 18%, referred to a circular cross         section test piece of diameter 12.5 mm.     -   YS/UTS ratio no higher than 0.90.     -   Maximum hardness (measured at 1.5 mm to 2.0 mm depth from the         pipe surface) not higher than 235 HV₁₀.     -   Minimum impact energy of 200 J/150 J (average/individual) and         minimum 85% of average shear area for both longitudinal and         transverse Charpy V-notch (CVN) tests performed on standard size         specimens or sub-size specimens when applicable at −40° C.         according with standard ASTM A 370.     -   Ductile-Brittle Transformation Temperature (ASTM E23) less than         or equal to about −60° C.     -   HIC resistance, assessed according with NACE Standard         TM0284-2003 Item No. 21215, using NACE solution A and test         duration 96 hours, with the following HIC parameters (average on         three sections of three specimens):         -   Crack Length Ratio, CLR≦10%         -   Crack Thickness Ratio, CTR≦3%         -   Crack Sensitivity Ratio, CSR≦0.5%     -   SSC resistance, assessed in accordance with ASTM G39, using NACE         TM0177 test solution A and a duration of 720 hours, with no         failure at 90% of the actual yield stress (AYS).

In order to achieve these results, the microstructural limitations about the ferrite content, at mid thickness (and possibly also at the inner surface of the pipe in the case of only external quenching), can be according to the following table:

X60Q X65Q X70Q Max. Ferrite 60%, preferably 40%, preferably 20%, preferably volume fraction 50% 30% 10%

Moreover, bends of grade X70Q and X65Q having a WT greater than or equal to 6 mm and less than or equal to 35 mm and the composition and microstructure discussed above can possess the same properties of the pipe of grade X70Q and X65Q, respectively, with maximum hardness (measured at 1.5 mm to 2 mm depth from the surface) not higher than 235 HV10, more preferably not higher than 230 HV10.

Instead, in some embodiments bends of grade X60Q having a WT greater than or equal to 6 mm and less than or equal to 35 mm and the composition and microstructure discussed above can possess the same properties of the pipe of grade X60Q, with maximum hardness (measured at 1.5 mm to 2 mm depth from the surface) not higher than 230 HV10, more preferably not higher than 225 HV10.

In some embodiments, the steel pipe can have the following chemical composition:

TABLE 2 Element P/O/I (*) Minimum Maximum C P 0.050 0.090 Mn P 0.90 1.30 Si P 0.10 0.35 Cr P 0.10 0.25 Ni P 0.08 0.30 Mo P 0.08 0.15 Nb O 0.000 0.035 Ti O 0.000 0.015 V O 0.000 0.040 Al P 0.020 0.040 N P 0.0030 0.0070 Cu I 0.00 0.20 S I 0.000 0.002 P I 0.000 0.015 Ca P 0.0008 0.0030 B I 0.000 0.0001 Zr O 0.000 0.010 Ta O 0.000 0.010 (*) P = Present; O = Optional; I = Impurity and can satisfy the following additional conditions: CE _(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range 0.26% to 0.37%; CE _(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.14% to 0.18%; P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]+50×(V+Nb) in the range of 10 to 14.5; P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)>2.0; Nb+V<0.07%, preferably <0.055%.

Advantageously the steel pipe, after the hot forming, can be subjected to the following steps:

-   -   cooling the steel pipe in air, preferably still air, up to reach         the room temperature;     -   heating the steel pipe, with a heating rate between 0.1° C./s         and 10° C./s, to an austenitizing temperature in the range         between 900° C. and 960° C., and providing a soaking time         between 180 s and 3600 s;     -   internal and external quenching (water quenching in a tank) of         the steel pipe, achieving a cooling rate of 20-80° C./s at mid         thickness and a cooling rate of 100-200° C./s in proximity of         the outer and inner surfaces of the pipe, in particular at 1.5-2         mm depth from said surfaces; or external quenching (by external         water jets rings) of the steel pipe, achieving a cooling rate of         20-80° C./s at mid thickness and at the inner surface of the         pipe, and a cooling rate of 100-200° C./s in proximity of the         outer surface of the pipe, in particular at 1.5-2 mm depth from         said outer surface;     -   heating the steel pipe, with a heating rate between 0.1° C./s         and 10° C./s, to a tempering temperature between 600° C. and         680° C. and providing a holding time at said tempering         temperature between 600 s and 5400 s.

Said embodiment of seamless steel pipe can comprise the following pipes:

-   -   grade X60Q steel pipes having a wall thickness higher than or         equal to 6 mm and lower than or equal to 35 mm, respecting the         conditions P2≧2.00 for wall thickness lower than 20 mm and         P2≧2.20 for wall thickness greater than or equal to 20 mm;     -   grade X65Q steel pipes having a wall thickness lower than 20 mm         respecting the condition P2≧2.10.

In some embodiments, the titanium content can be in the range 0.006-0.0015%.

In some embodiments, steel pipes can have the following chemical composition:

TABLE 3 Element P/O/I (*) Minimum Maximum C P 0.060 0.090 Mn P 0.95 1.30 Si P 0.10 0.35 Cr P 0.10 0.30 Ni P 0.20 0.40 Mo P 0.14 0.25 Nb O 0.000 0.035 Ti O 0.000 0.015 V O 0.000 0.040 Al P 0.020 0.040 N P 0.0030 0.0070 Cu I 0.00 0.20 S I 0.000 0.002 P I 0.000 0.015 Ca P 0.0008 0.0030 B I 0.000 0.0001 Zr O 0.000 0.010 Ta O 0.000 0.010 (*) P = Present; O = Optional; I = Impurity and can satisfy the following additional conditions: CE _(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range 0.36% to 0.43%; CE _(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.18% to 0.21%; P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]+50×(V+Nb) in the range of 10 to 14.5; P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)>2.30; Nb+V<0.07%, preferably <0.055%.

Advantageously the steel pipe, after the hot forming, can be subjected to the following steps:

-   -   cooling the steel pipe in air, preferably still air, up to reach         the room temperature;     -   heating the steel pipe, with a heating rate between 0.1° C./s         and 10° C./s, to an austenitizing temperature in the range         between 900° C. and 960° C., and providing a soaking time         between 180 s and 3600 s;     -   internal and external quenching of the steel pipe (water         quenching in a tank), achieving a cooling rate of 20-80° C./s at         mid thickness and a cooling rate of 100-200° C./s in proximity         of the outer and inner surfaces of the pipe, in particular at         1.5-2 mm depth from said surfaces;     -   heating the steel pipe, with a heating rate between 0.1° C./s         and 10° C./s, to a tempering temperature between 600° C. and         680° C. and providing a holding time at said tempering         temperature between 600 s and 5400 s.

Said second preferred embodiment of seamless steel pipes comprises:

-   -   X65Q steel pipes having a wall thickness higher than or equal to         20 mm and lower than 35 mm.

In some embodiments, the titanium content can be in the range 0.006-0.0015%.

In certain embodiments, the steel pipe can have the following chemical composition:

TABLE 4 Element P/O/I (*) Minimum Maximum C P 0.060 0.090 Mn P 0.95 1.30 Si P 0.10 0.35 Cr P 0.20 0.40 Ni P 0.25 0.40 Mo P 0.25 0.35 Nb O 0.020 0.035 Ti O 0.000 0.015 V O 0.000 0.010 Al P 0.020 0.040 N P 0.0030 0.0070 Cu I 0.00 0.20 S I 0.000 0.002 P I 0.000 0.015 Ca P 0.0008 0.0030 B I 0.000 0.0001 Zr O 0.000 0.010 Ta O 0.000 0.010 (*) P = Present; O = Optional; I = Impurity and can satisfy the following additional conditions: CE _(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range 0.37% to 0.43%; CE _(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.18% to 0.21%; P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]+50×(V+Nb) in the range of 12 to 14.5; P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)≧2.30.

Advantageously the steel pipe, after the hot forming, can be subjected to the following steps:

-   -   cooling the steel pipe in air, preferably still air, up to reach         the room temperature;     -   heating the steel pipe, with a heating rate between 0.1° C./s         and 10° C./s, to an austenitizing temperature in the range         between 900° C. and 960° C., and providing a soaking time         between 180 s and 3600 s;     -   internal and external quenching (water quenching in a tank) of         the steel pipe achieving a cooling rate of 20-80° C./s at mid         thickness and a cooling rate of 100-200° C./s in proximity of         the outer and inner surfaces of the pipe, in particular at 1.5-2         mm depth from said surfaces; or external quenching (by external         water jets rings) of the steel pipe, achieving a cooling rate of         20-80° C./s at mid thickness and at the inner surface of the         pipe, and a cooling rate of 100-200° C./s in proximity of the         outer surface of the pipe, in particular at 1.5-2 mm depth from         said outer surface;     -   heating the steel pipe, with a heating rate between 0.1° C./s         and 10° C./s, to a tempering temperature between 600° C. and         680° C. and providing a holding time at said tempering         temperature between 600 s and 5400 s.

Said embodiment of seamless steel pipe can comprise:

-   -   X70Q steel pipes having a wall thickness higher than or equal to         6 mm and lower than 35 mm with P2≧2.35 for wall thickness lower         than 20 mm and P2≧2.45 for wall thickness greater than or equal         to 20 mm;     -   X65Q steel pipes having a wall thickness higher than or equal to         20 mm and lower than 35 mm with the condition P2≧2.3.

In some embodiments, the titanium content can be in the range 0.006-0.0015%.

In some embodiments, steel pipe can have the following chemical composition:

TABLE 5 Element P/O/I (*) Minimum Maximum C P 0.060 0.090 Mn P 0.90 1.20 Si P 0.10 0.35 Cr P 0.10 0.25 Ni P 0.05 0.20 Mo P 0.05 0.15 Nb O 0.000 0.005 Ti O 0.005 0.015 V O 0.000 0.070 Al P 0.020 0.040 N P 0.0030 0.0070 Cu I 0.00 0.20 S I 0.000 0.002 P I 0.000 0.015 Ca P 0.0008 0.0030 B I 0.000 0.0001 Zr O 0.000 0.010 Ta O 0.000 0.010 (*) P = Present; O = Optional; I = Impurity and satisfy the following additional conditions: CE _(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range 0.26% to 0.36%; CE _(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.14% to 0.18%; P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]+50×(V+Nb) in the range of 10 to 14.5; P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)>2.00; Nb+V<0.07%, preferably <0.055%.

Advantageously the steel pipe, after the hot forming, can be subjected to the following steps:

-   -   cooling the steel pipe in air, preferably still air, up to reach         the room temperature;     -   heating the steel pipe, with a heating rate between 0.1° C./s         and 10° C./s, to an austenitizing temperature in the range         between 900° C. and 950° C., and providing a soaking time         between 180 s and 3600 s;     -   internal and external quenching (water quenching in a tank) of         the steel pipe achieving a cooling rate of 20-80° C./s at mid         thickness and a cooling rate of 100-200° C./s in proximity of         the outer and inner surfaces of the pipe, in particular at 1.5-2         mm depth from said surfaces; or external quenching (by external         water jets rings) of the steel pipe, achieving a cooling rate of         20-80° C./s at mid thickness and at the inner surface of the         pipe, and a cooling rate of 100-200° C./s in proximity of the         outer surface of the pipe, in particular at 1.5-2 mm depth from         said outer surface;     -   heating the steel pipe, with a heating rate between 0.1° C./s         and 10° C./s, to a tempering temperature between 600° C. and         680° C. and providing a holding time at said tempering         temperature between 900 s and 5400 s.

Said fourth preferred embodiment of seamless steel pipes comprises:

-   -   grade X60Q steel pipes having a wall thickness higher than or         equal to 6 mm and lower than or equal to 35 mm, respecting the         conditions P2≧2.00 for wall thickness lower than 20 mm and         P2≧2.20 for wall thickness greater than or equal to 20 mm.     -   grade X65Q, steel pipes having a wall thickness lower than 20 mm         respecting the condition P2≧2.10.

In some embodiments, steel pipes can have the following chemical composition:

TABLE 6 Element P/O/I (*) Minimum Maximum C P 0.060 0.090 Mn P 0.95 1.30 Si P 0.10 0.35 Cr P 0.10 0.40 Ni P 0.05 0.40 Mo P 0.07 0.25 Nb O 0.000 0.005 Ti O 0.005 0.015 V O 0.000 0.070 Al P 0.020 0.040 N P 0.0030 0.0070 Cu I 0.00 0.20 S I 0.000 0.002 P I 0.000 0.015 Ca P 0.0008 0.0030 B I 0.000 0.0001 Zr O 0.000 0.010 Ta O 0.000 0.010 (*) P = Present; O = Optional; I = Impurity and can satisfy the following additional conditions: CE _(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15) in the range 0.31% to 0.41%; CE _(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.15% to 0.20%; P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]+50×(V+Nb) in the range of 11 to 14.5; P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)≧2.30; Nb+V<0.07%, preferably <0.055%.

Advantageously the steel pipe, after the hot forming, can be subjected to the following steps:

-   -   cooling the steel pipe in air, preferably still air, up to reach         the room temperature;     -   heating the steel pipe, with a heating rate between 0.1° C./s         and 10° C./s, to an austenitizing temperature in the range         between 900° C. and 950° C., and providing a soaking time         between 300 s and 3600 s;     -   internal and external quenching (water quenching in a tank)         achieving a cooling rate of 20-80° C./s at mid thickness and a         cooling rate of 100-200° C./s in proximity of the outer and         inner surfaces of the pipe, in particular at 1.5-2 mm depth from         said surfaces;     -   heating the steel pipe, with a heating rate between 0.1° C./s         and 10° C./s, to a tempering temperature between 600° C. and         680° C. and providing a holding time at said tempering         temperature between 900 s and 5400 s.

Said embodiment of seamless steel pipe can comprise:

-   -   X65Q steel pipes having a wall thickness higher than or equal to         20 mm and lower than 35 mm.

In some embodiments, the steel pipes can have the following chemical composition:

TABLE 7 Element P/O/I (*) Minimum Maximum C P 0.060 0.085 Mn P 1.00 1.30 Si P 0.10 0.30 Cr P 0.20 0.40 Ni P 0.20 0.40 Mo P 0.10 0.25 Nb O 0.000 0.005 Ti O 0.005 0.015 V O 0.000 0.070 Al P 0.020 0.040 N P 0.0030 0.0070 Cu I 0.00 0.15 S I 0.000 0.0015 P I 0.000 0.012 Ca P 0.0008 0.0030 B I 0.000 0.0001 Zr O 0.000 0.010 Ta O 0.000 0.010 (*) P = Present; O = Optional; I = Impurity and can satisfy the following additional conditions: CE _(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range 0.37% to 0.43%; CE _(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.16% to 0.22%; P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]+50×(V+Nb) in the range of 12.5 to 14.5; P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)≧2.30; Nb+V<0.07%, preferably <0.055%.

Advantageously the steel pipe, after the hot forming, can be subjected to the following steps:

-   -   cooling the steel pipe in air, preferably still air, up to reach         the room temperature;     -   heating the steel pipe, with a heating rate between 0.1° C./s         and 10° C./s, to an austenitizing temperature in the range         between 900° C. and 950° C., and providing a soaking time         between 300 s and 3600 s;     -   internal and external quenching (water quenching in a tank)         achieving a cooling rate of 20-80° C./s at mid thickness and a         cooling rate of 100-200° C./s in proximity of the outer and         inner surfaces of the pipe, in particular at 1.5-2 mm depth from         said surfaces;     -   heating the steel pipe, with a heating rate between 0.1° C./s         and 10° C./s, to a tempering temperature between 600° C. and         680° C. and providing a holding time at said tempering         temperature between 900 s and 5400 s.

Said embodiment of seamless steel pipes can comprise:

-   -   X70Q steel pipes having a wall thickness higher than or equal to         6 mm and lower than 35 mm with P2≧2.35 for wall thickness lower         than 20 mm and P2≧2.45 for wall thickness greater than or equal         to 20 mm.     -   X65Q steel pipes having a wall thickness higher than or equal to         20 mm and lower than 35 mm with the condition P2≧2.30.

EXAMPLES

Below some examples according to the present disclosure are disclosed. In each example the chemical composition of the selected steel, the process parameters regarding the steps of austenitizing, quenching and tempering, the microstructure along the wall thickness of the pipe and the maximum hardness value detected along the whole thickness of the pipe are indicated. In all the examples the maximum hardness value is below 235 HV₁₀, and yield strength, toughness and corrosion resistance satisfy at least one of the grades X60Q, X65Q and X70Q.

The methodology used for the characterization of the Q&T pipes and bends is here summarized:

The microstructural constituents through the wall thickness were analysed by optical microscopy after Nital 2% etching. The prior austenitic grain size was measured after polishing and etching with Winsteard solution, based on picric acid in saturated H₂O solution. The grain size was measured according to ASTM E112 mean lineal intercept method, hereby incorporated by reference in its entirety.

High angle domains (packet size) were analysed by Electron back scattering diffraction (EBSD), applying the ASTM E112 mean linear intercept method to determine the average packet size.

Hydrogen Induced Cracking (HIC) test were carried out according to NACE TM 02-84/2011 Standard, hereby incorporated by reference in its entirety.

The four point bend test (FPBT) was carried out according to the standard ASTM G39, hereby incorporated by reference in its entirety, using NACE TM 02-84/2011 Solution A, hereby incorporated by reference in its entirety.

The tensile tests were carried out according to ASTM A 370, hereby incorporated by reference in its entirety, using strip or round specimens ½ inch diameter taken from mid thickness in both longitudinal and transverse direction.

Toughness was tested by Charpy V-Notch impact tests, carried out according to ASTM A370, hereby incorporated by reference in its entirety. The specimens were taken either from mid thickness either at 2 mm from the outer diameter in transverse direction. Temperatures between −40° C. and −120° C. were tested and the 50% fracture appearance transition temperature (FATT) was used as a parameter to characterize material toughness.

Hardness was tested with four indentations per sector at 1.5 mm (−0 to +0.5 mm) from OD (outer diameter), at mid thickness and at 1.5 mm (−0 to +0.5 mm) from ID (inner diameter), following ISO 3183 and DNV-OS-F101 specifications, hereby incorporated by reference in their entirety. Four specimens taken at 90° along the circumference from both tail and head of three tubes per heat treatment lot were tested.

The mechanical properties after strain ageing were carried out after the application of multiple straining cycles to full thickness large specimens, that subsequently underwent ageing treatments according to DNV offshore F101, at 250° C. for 1 h. The straining cycles were composed of the following steps: a) Compression to −3% absolute strain, b) Unloading to 0 stress, c) Tension till+3% relative strain, d) Unloading to 0 stress, e) repetition five times of steps a) to d), ending in tension. The full thickness specimens were subsequently machined to prepare the tensile, Charpy, HIC and FPBT specimens.

Example 1

A steel with the following chemical composition has been selected:

-   -   0.08% C, 1.04% Mn, 0.24% Si, 0.12% Cr, 0.26% Ni, 0.13% Mo,         0.025% Al, 0.0008% Ca, 0.020% Nb, 0.002% Ti, 0.03% V, 0.0045% N,         the remaining being iron and impurities;     -   said impurities being 0.17% Cu, 0.0020% S, 0.0012% P, 0.0002% B;     -   and being P1=13.7; P2=2.24; CE_(IIW)=0.34%; and CE_(PCM)=0.17%.

A seamless steel pipe has been hot formed, having a wall thickness of 20 mm.

Said hot formed steel pipe has been subjected to the following steps:

-   -   cooling the steel pipe in air, preferably still air, up to reach         the room temperature;     -   heating the steel pipe, with a heating rate of 0.3° C./s, to an         austenitizing temperature of 920° C. and providing a soaking         time of 1200 s;     -   quenching in a tank, achieving a cooling rate of about 50° C./s         at mid thickness and a cooling rate of about 120° C./s in         proximity of the outer and inner surfaces of the pipe, in         particular at 1.5-2 mm depth from said surfaces;     -   heating the steel pipe, with a heating rate of 0.2° C./s, to a         tempering temperature of 635° C. and providing a holding time of         2400 s at said tempering temperature.

The resulting average microstructure of the steel pipe comprises, in volume percentage:

-   -   at mid thickness, tempered bainite equal to about 65% and         ferrite (V_(F)) equal to about 35%,     -   at a distance up to 2 mm starting from outer and inner surfaces         of the steel pipe, tempered martensite equal to about 10%,         ferrite equal to 10% and tempered bainite equal to about 80%.

The average prior austenite grain size, measured according to ASTM E112, is equal to 14 μm. The packet size is equal to 5.5 μm.

The maximum hardness value, measured at 1.5-2.0 mm depth from the outer and inner surfaces, is equal to 212 HV₁₀ (<225 HV₁₀).

The minimum and maximum yield strength values were equal to 446 MPa and 483 MPa, respectively.

The minimum and maximum tensile strength values were equal to 536 MPa and 584 MPa, respectively.

The minimum and maximum elongation values % after rupture were equal to 29.6% and 34.1%, respectively.

The average impact energy at −60° C. was 331 J, with a minimum value of 326 J and an average shear area of 100%.

The average 50% FATT was at −105° C.

Hydrogen Induced cracking tests passed with CLR %=0%, CTR %=0% and CSR %=0%.

Four point bend tests at 90% of SMYS passed with no failures after 720 h of tests.

This steel pipe satisfies the grade X60Q.

Example 2

A steel with the following chemical composition has been selected:

-   -   0.08% C, 1.10% Mn, 0.27% Si, 0.14% Cr, 0.15% Ni, 0.09% Mo,         0.029% Al, 0.0014% Ca, 0.001% Nb, 0.011% Ti, 0.04% V, 0.0048% N,         the remaining being iron and impurities;     -   said impurities being 0.17% Cu, 0.0012% S, 0.013% P, 0.0001% B;     -   and being P1=12.8; P2=2.32; CE_(IIW)=0.34%; and CE_(PCM)=0.17%.

A seamless steel pipe has been hot formed, having a wall thickness of 20 mm.

Said hot formed steel pipe has been subjected to the following steps:

-   -   cooling the steel pipe in air, preferably still air, up to reach         the room temperature;     -   heating the steel pipe, with a heating rate of 0.3° C./s, to an         austenitizing temperature of 920° C. and providing a soaking         time of 1200 s;     -   quenching in a tank, achieving a cooling rate of about 50° C./s         at mid thickness and a cooling rate of about 130° C./s in         proximity of the outer and inner surfaces of the pipe, in         particular at 1.5-2 mm depth from said surfaces;     -   heating the steel pipe, with a heating rate of 0.25° C./s, to a         tempering temperature of 635° C. and providing a holding time of         2400 sec at said tempering temperature.

The resulting average microstructure of the steel pipe comprises, in volume percentage:

at mid thickness, tempered bainite equal to about 90% and ferrite equal to about 10%;

at a distance up to 2 mm starting from outer and inner surfaces of the steel pipe, tempered martensite equal to about 40% and tempered bainite equal to about 60%.

The average prior austenite grain size, measured according to ASTM E112, is equal to 22 μm. The packet size is equal to 6.5 μm.

The maximum hardness value, measured at 1.5-2.0 mm depth from the outer and inner surfaces, is equal to 218 HV₁₀ (<225 HV₁₀).

The minimum and maximum yield strength values were equal to 432 MPa and 454 MPa, respectively

The minimum and maximum tensile strength value were equal to 540 and 574 MPa, respectively.

The minimum and maximum elongation % after rupture was 24% and 30%.

The average impact energy at −60° C. was 324 J, with a minimum value of 282 J. The average shear area was 98% with a minimum shear area of 90%.

Hydrogen Induced cracking tests passed with CLR %=0%, CTR %=0% and CSR=0%.

Four point bend tests at 90% of SMYS passed with no failures after 720 h of tests.

This steel pipe satisfies the grade X60Q.

Example 3

A steel with the following chemical composition has been selected:

-   -   0.075% C, 1.01% Mn, 0.27% Si, 0.38% Cr, 0.30% Ni, 0.33% Mo,         0.031% Al, 0.0010% Ca, 0.024% Nb, 0.005% Ti, 0.003% V, 0.0047%         N, the remaining being iron and impurities; said impurities         being 0.09% Cu, 0.001% S, 0.011% P, 0.0002% B;     -   and being P1=14.2; P2=2.50; CE_(IIW)=0.41%; and CE_(PCM)=0.19%.

A seamless steel pipe has been hot formed, having a wall thickness of 25 mm.

Said hot formed steel pipe has been subjected to the following steps:

-   -   cooling the steel pipe in air, preferably still air, up to reach         the room temperature;     -   heating the steel pipe, with a heating rate of 0.3° C./s, to an         austenitizing temperature of 920° C. and providing a soaking         time of 1200 s;     -   quenching in a tank, achieving a cooling rate of 35° C./s at mid         thickness and a cooling rate of about 130° C./s in proximity of         the outer and inner surfaces of the pipe, in particular at 1.5-2         mm depth from said surfaces;     -   heating the steel pipe, with a heating rate of 0.2° C./s, to a         tempering temperature of 650° C. and providing a holding time of         2400 sec at said tempering temperature.

The resulting average microstructure of the steel pipe comprises, in volume percentage:

-   -   at mid thickness, tempered bainite equal to about 100%;     -   at a distance up to 2 mm starting from outer and inner surfaces         of the steel pipe, tempered martensite equal to about 50% and         tempered bainite equal to about 50%.

The average prior austenite grain size, measured according to ASTM E112, is equal to 23 μm. The packet size is equal to 5.7 μm.

The maximum hardness value, measured at 1.5-2.0 mm depth from the outer and inner surfaces, is equal to 230 HV₁₀ (<235 HV₁₀).

The minimum and maximum yield strength values were equal to 513 MPa and 559 MPa, respectively.

The minimum and maximum tensile strength value were equal to 599 and 638 MPa, respectively.

The minimum and maximum elongation % after rupture was 30% and 32%.

The average impact energy at −60° C. was 337 J, with a minimum value of 190 J. The average shear area was 99% with a minimum shear area of 70%.

The average 50% FATT was at −100° C.

After strain ageing the measured yield strength value was 551 MPa, the tensile strength value was 622 MPa, the yield to tensile ratio was 0.88, the elongation value was 34% and the average 50% FATT was at −100° C. All the mechanical properties were compliant with the grade X70, either before either after strain ageing.

Hydrogen Induced cracking tests passed with CLR %=0%, CTR %=0% and CSR %=0%, either in the Q&T material either in the strained and aged material.

Four point bend tests at 90% of SMYS passed with no failures after 720 h of tests, either in the Q&T material either in the strained and aged material.

This steel pipe satisfies the grade X70Q.

Example 4

A steel with the following chemical composition has been selected:

-   -   0.076% C, 1.15% Mn, 0.25% Si, 0.14% Cr, 0.22% Ni, 0.12% Mo,         0.031% Al, 0.0013% Ca, 0.024% Nb, 0.002% Ti, 0.007% V, 0.0048%         N, the remaining being iron and impurities;     -   said impurities being 0.16% Cu, 0.0012% S, 0.013% P, 0.0001% B;     -   and being P1=13.6; P2=2.30; CE_(IIW)=0.35%; and CE_(PCM)=0.17%.

A seamless steel pipe has been hot formed, having a wall thickness of 11 mm.

Said hot formed steel pipe has been subjected to the following steps:

-   -   cooling the steel pipe in air, preferably still air, up to reach         the room temperature;     -   heating the steel pipe, with a heating rate of 0.4° C./s, to an         austenitizing temperature of 920° C. and providing a soaking         time of 600 s;     -   external quenching by water rings, achieving a cooling rate of         about 50° C./s at mid thickness and also at the inner surface of         the pipe, and a cooling rate of about 130° C./s in proximity of         the outer surface of the pipe, in particular at 1.5-2 mm depth         from said outer surface;     -   heating the steel pipe, with a heating rate of 0.25° C./s, to a         tempering temperature of 620° C. and providing a holding time of         2400 sec at said tempering temperature.

The resulting average microstructure of the steel pipe comprises, in volume percentage:

-   -   at mid thickness and at the inner surface of the pipe, tempered         bainite equal to about 65% and ferrite equal to about 35%;     -   at a distance up to 2 mm starting from outer surface of the         steel pipe, tempered martensite equal to about 50%, tempered         bainite equal to about 45% and fine polygonal ferrite equal to         about 5%.

The average prior austenite grain size, measured according to ASTM E112, is equal to 16 μm. The packet size is equal to 6.0 μm.

The maximum hardness value, measured at 1.5-2.0 mm depth from the outer and inner surfaces, is equal to 218 HV₁₀ (<230 HV₁₀).

The minimum and maximum yield strength values were equal to 448 MPa and 518 MPa, respectively.

The minimum and maximum tensile strength value were equal to 539 and 592 MPa, respectively.

The minimum and maximum elongation % after rupture was 29.8% and 34.2%.

The average impact energy at −60° C. was 348 J, with a minimum value of 246 J. The average shear area was 96% with a minimum shear area of 80%. At −40° C. the minimum impact energy was 304 J, with a minimum shear area of 100%.

Hydrogen Induced cracking tests passed with CLR %=0%, CTR %=0% and CSR=0%.

Four point bend tests at 90% of SMYS passed with no failures after 720 h of tests.

This steel pipe satisfies the grade X60Q.

Example 5

A steel with the following chemical composition has been selected:

-   -   0.084% C, 1.15% Mn, 0.25% Si, 0.16% Cr, 0.30% Ni, 0.18% Mo,         0.025% Al, 0.0010% Ca, 0.025% Nb, 0.002% Ti, 0.03% V, 0.0055% N,         the remaining being iron and impurities;     -   said impurities being 0.12% Cu, 0.001% S, 0.011% P, 0.0001% B;     -   and being P1=14.0; P2=2.48; CE_(IIW)=0.38%; and CE_(PCM)=0.18%.

A seamless steel pipe has been hot formed, having a wall thickness of 31.8 mm.

Said hot formed steel pipe has been subjected to the following steps:

-   -   cooling the steel pipe in air, preferably still air, up to reach         the room temperature;     -   heating the steel pipe, with a heating rate of 0.2° C./s, to an         austenitizing temperature of 920° C. and providing a soaking         time of 600 s;     -   quenching in a tank, achieving a cooling rate of about 20° C./s         at mid thickness and a cooling rate of about 140° C./s in         proximity of the outer and inner surfaces of the pipe, in         particular at 1.5-2 mm depth from said surfaces;     -   heating the steel pipe, with a heating rate of 0.2° C./s, to a         tempering temperature of 640° C. and providing a holding time of         3600 sec at said tempering temperature.

The resulting average microstructure of the steel pipe comprises, in volume percentage:

-   -   at mid thickness, tempered bainite equal to about 75% and         ferrite equal to about 25%;     -   at a distance up to 2 mm starting from outer and inner surfaces         of the steel pipe, tempered martensite equal to about 60% and         tempered bainite equal to about 40%.

The average prior austenite grain size, measured according to ASTM E112, is equal to 15 μm. The packet size is equal to 5.8 μm.

The maximum hardness value, measured at 1.5-2.0 mm depth from the outer and inner surfaces, is equal to 228 HV₁₀ (<230 HV₁₀).

The minimum and maximum yield strength values were equal to 480 MPa and 501 MPa, respectively.

The minimum and maximum tensile strength value were equal to 578 and 590 MPa, respectively.

The minimum and maximum elongation % after rupture was 28% and 33%.

The average impact energy at −60° C. was 335 J, with a minimum value of 290 J. The average shear area was 98% with a minimum shear area of 90%.

Hydrogen Induced cracking tests passed with CLR %=0%, CTR %=0% and CSR=0%.

Four point bend tests at 90% of SMYS passed with no failures after 720 h of tests.

This steel pipe satisfies the grade X65Q.

Example 6

A steel with the following chemical composition has been selected:

-   -   0.081% C, 0.94% Mn, 0.24% Si, 0.11% Cr, 0.05% Ni, 0.069% Mo,         0.029% Al, 0.0012% Ca, 0.012% Ti, 0.054% V, 0.0052% N, the         remaining being iron and impurities;     -   said impurities being 0.11% Cu, 0.0012% S, 0.010% P;     -   and being P1=13.7; P2=2.12; CE_(IIW)=0.29%; and CE_(PCM)=0.16%.

A seamless steel pipe has been hot formed, having a wall thickness of 12.7 mm.

Said hot formed steel pipe has been subjected to the following steps:

-   -   cooling the steel pipe in air, preferably still air, up to reach         the room temperature;     -   heating the steel pipe, with a heating rate of 0.4° C./s, to an         austenitizing temperature of 900° C. and providing a soaking         time of 900 s;     -   quenching in a tank, achieving a cooling rate of about 75° C./s         at mid thickness and a cooling rate of about 100° C./s in         proximity of the outer and inner surfaces of the pipe, in         particular at 1.5-2 mm depth from said surfaces;     -   heating the steel pipe, with a heating rate of 0.23° C./s, to a         tempering temperature of 640° C. and providing a holding time of         2700 sec at said tempering temperature.

The resulting average microstructure of the steel pipe comprises, in volume percentage:

-   -   at mid thickness, tempered bainite equal to about 50% and         ferrite equal to about 50%;     -   at a distance up to 2 mm starting from outer and inner surfaces         of the steel pipe, tempered martensite equal to about 10%,         tempered bainite equal to about 80% and ferrite equal to about         10%.

The average prior austenite grain size, measured according to ASTM E112, is equal to 15-17 μm.

The maximum hardness value, measured at 1.5-2.0 mm depth from the outer and inner surfaces, is equal to 196 HV₁₀ (<225 HV₁₀)

The minimum and maximum yield strength values were equal to 440 MPa and 487 MPa, respectively.

The minimum and maximum tensile strength value were equal to 529 and 565 MPa, respectively.

The minimum and maximum elongation % after rupture was 38% and 45%.

The average impact energy at −50° C. was 326 J, with a minimum value of 253 J. The average shear area was 100% with a minimum shear area of 100%.

Hydrogen Induced cracking tests passed with CLR %=0%, CTR %=0% and CSR=0%.

Four point bend tests at 90% of AYS passed with no failures after 720 h of tests.

This steel pipe satisfies the grade X60Q.

Example 7

A steel with the following chemical composition has been selected:

-   -   0.085% C, 0.93% Mn, 0.24% Si, 0.16% Cr, 0.05% Ni, 0.085% Mo,         0.030% Al, 0.0011% Ca, 0.011% Ti, 0.053% V, 0.0050% N, the         remaining being iron and impurities;     -   said impurities being 0.127% Cu, 0.0016% S, 0.008% P; and being         P1=13.9; P2=2.21; CE_(IIW)=0.31%; and CE_(PCM)=0.17%.

A seamless steel pipe has been hot formed, having a wall thickness of 15.9 mm.

Said hot formed steel pipe has been subjected to the following steps:

-   -   cooling the steel pipe in air, preferably still air, up to reach         the room temperature;     -   heating the steel pipe, with a heating rate of 0.3° C./s, to an         austenitizing temperature of 900° C. and providing a soaking         time of 900 s;     -   quenching in a tank, achieving a cooling rate of about 65° C./s         at mid thickness and a cooling rate of about 100° C./s in         proximity of the outer and inner surfaces of the pipe, in         particular at 1.5-2 mm depth from said surfaces;     -   heating the steel pipe, with a heating rate of 0.15° C./s, to a         tempering temperature of 635° C. and providing a holding time of         2700 sec at said tempering temperature.

The resulting average microstructure of the steel pipe comprises, in volume percentage:

-   -   at mid thickness, tempered bainite equal to about 65% and         ferrite equal to about 35%; at a distance up to 2 mm starting         from outer and inner surfaces of the steel pipe, tempered         martensite equal to about 10%, tempered bainite equal to about         80% and ferrite equal to about 10%.

The average prior austenite grain size, measured according to ASTM E112, is equal to 15-17 μm.

The maximum hardness value, measured at 1.5-2.0 mm depth from the outer and inner surfaces, is equal to 228 HV₁₀ (<230 HV₁₀)

The minimum and maximum yield strength values were equal to 459 MPa and 490 MPa, respectively.

The minimum and maximum tensile strength value were equal to 543 and 574 MPa, respectively.

The minimum and maximum elongation % after rupture was 45% and 47%.

The average impact energy at −50° C. was 329 J, with a minimum value of 287 J. The average shear area was 97% with a minimum shear area of 85%.

Hydrogen Induced cracking tests passed with CLR %=0%, CTR %=0% and CSR=0%.

Four point bend tests at 90% of AYS passed with no failures after 720 h of tests.

This steel pipe satisfies the grade X65Q.

Example 8

A steel with the following chemical composition has been selected:

-   -   0.06% C, 1.24% Mn, 0.26% Si, 0.30% Cr, 0.26% Ni, 0.112% Mo,         0.029% Al, 0.0014% Ca, 0.012% Ti, 0.059% V, 0.0058% N, the         remaining being iron and impurities;     -   said impurities being 0.10% Cu, 0.0005% S, 0.008% P;     -   and being P1=12.7; P2=2.52; CE_(IIW)=0.38%; and CE_(PCM)=0.17%.

A seamless steel pipe has been hot formed, having a wall thickness of 25.4 mm.

Said hot formed steel pipe has been subjected to the following steps:

-   -   cooling the steel pipe in air, preferably still air, up to reach         the room temperature;     -   heating the steel pipe, with a heating rate of 0.3° C./s, to an         austenitizing temperature of 900° C. and providing a soaking         time of 900 s;     -   quenching in a tank, achieving a cooling rate of about 30° C./s         at mid thickness and a cooling rate of about 100° C./s in         proximity of the outer and inner surfaces of the pipe, in         particular at 1.5-2 mm depth from said surfaces;     -   heating the steel pipe, with a heating rate of 0.15° C./s, to a         tempering temperature of 650° C. and providing a holding time of         2700 sec at said tempering temperature.

The resulting average microstructure of the steel pipe comprises, in volume percentage:

-   -   at mid thickness, tempered bainite equal to about 70% and         ferrite equal to about 30%;     -   at a distance up to 2 mm starting from outer and inner surfaces         of the steel pipe, tempered martensite equal to about 10%,         tempered bainite equal to about 80% and ferrite equal to about         10%.

The average prior austenite grain size, measured according to ASTM E112, is equal to 15-17 μm.

The maximum hardness value, measured at 1.5-2.0 mm depth from the outer and inner surfaces, is equal to 219 HV₁₀ (<230 HV₁₀)

The minimum and maximum yield strength values were equal to 476 MPa and 508 MPa, respectively.

The minimum and maximum tensile strength value were equal to 558 and 589 MPa, respectively.

The minimum and maximum elongation % after rupture was 54% and 60%.

The average impact energy at −40° C. was 433 J, with a minimum value of 461 J. The average shear area was 100% with a minimum shear area of 100%.

The 50% FATT was below −70° C.

Hydrogen Induced cracking tests passed with CLR %=0%, CTR %=0% and CSR=0%.

Four point bend tests at 90% of AYS passed with no failures after 720 h of tests.

This steel pipe satisfies the grade X65Q.

Example 9

A steel with the following chemical composition has been selected:

-   -   0.06% C, 1.30% Mn, 0.25% Si, 0.35% Cr, 0.38% Ni, 0.139% Mo,         0.025% Al, 0.0018% Ca, 0.012% Ti, 0.059% V, 0.0068% N, the         remaining being iron and impurities;     -   said impurities being 0.137% Cu, 0.0011% S, 0.013% P;     -   and being P1=12.8; P2=2.67; CE_(IIW)=0.42%; and CE_(PCM)=0.18%.

A seamless steel pipe has been hot formed, having a wall thickness of 30 mm.

Said hot formed steel pipe has been subjected to the following steps:

-   -   cooling the steel pipe in air, preferably still air, up to reach         the room temperature;     -   heating the steel pipe, with a heating rate of 0.35° C./s, to an         austenitizing temperature of 900° C. and providing a soaking         time of 900 s;     -   quenching in a tank, achieving a cooling rate of about 25° C./s         at mid thickness and a cooling rate of about 100° C./s in         proximity of the outer and inner surfaces of the pipe, in         particular at 1.5-2 mm depth from said surfaces;     -   heating the steel pipe, with a heating rate of 0.15° C./s, to a         tempering temperature of 635° C. and providing a holding time of         3600 sec at said tempering temperature.

The resulting average microstructure of the steel pipe comprises, in volume percentage:

-   -   at mid thickness, tempered bainite equal to about 90% and         ferrite equal to about 10%;     -   at a distance up to 2 mm starting from outer and inner surfaces         of the steel pipe, tempered martensite equal to about 5-10%,         tempered bainite equal to about 90% and ferrite equal to about         0-5%.

The average prior austenite grain size, measured according to ASTM E112, is equal to 15-20 μm.

The maximum hardness value, measured at 1.5-2.0 mm depth from the outer and inner surfaces, is equal to 234 HV₁₀ (<235 HV₁₀).

The minimum and maximum yield strength values were equal to 506 MPa and 523 MPa, respectively.

The minimum and maximum tensile strength value were equal to 592 and 609 MPa, respectively.

The minimum and maximum elongation % after rupture was 29% and 31%. (round specimen)

The average impact energy at −40° C. was 450 J, with a minimum value of 425 J. The average shear area was 100% with a minimum shear area of 100%.

The 50% FATT was below −60° C.

Hydrogen Induced cracking tests passed with CLR %=0%, CTR %=0% and CSR=0%.

Four point bend tests at 90% of AYS passed with no failures after 720 h of tests.

This steel pipe satisfies the grade X70Q.

Example 10

A steel with the following chemical composition has been selected:

-   -   0.06% C, 1.30% Mn, 0.27% Si, 0.35% Cr, 0.38% Ni, 0.21% Mo,         0.025% Al, 0.0017% Ca, 0.012% Ti, 0.059% V, 0.0055% N, the         remaining being iron and impurities;     -   said impurities being 0.127% Cu, 0.0007% S, 0.011% P; and being         P1=13.2; P2=2.72; CE_(IIW)=0.43%; and CE_(PCM)=0.18%.

A seamless steel pipe has been hot formed, having a wall thickness of 32.5 mm.

Said hot formed steel pipe has been subjected to the following steps:

-   -   cooling the steel pipe in air, preferably still air, up to reach         the room temperature;     -   heating the steel pipe, with a heating rate of 0.38° C./s, to an         austenitizing temperature of 900° C. and providing a soaking         time of 900 s;     -   quenching in a tank, achieving a cooling rate of about 23° C./s         at mid thickness and a cooling rate of about 100° C./s in         proximity of the outer and inner surfaces of the pipe, in         particular at 1.5-2 mm depth from said surfaces;     -   heating the steel pipe, with a heating rate of 0.15° C./s, to a         tempering temperature of 660° C. and providing a holding time of         3600 sec at said tempering temperature.

The resulting average microstructure of the steel pipe comprises, in volume percentage:

-   -   at mid thickness, tempered bainite equal to about 95% and         ferrite equal to about 5%;     -   at a distance up to 2 mm starting from outer and inner surfaces         of the steel pipe, tempered martensite equal to about 5-10%,         tempered bainite equal to about 90% and ferrite equal to about         0-5%.

The average prior austenite grain size, measured according to ASTM E112, is equal to 15-20 μm.

The maximum hardness value, measured at 1.5-2.0 mm depth from the outer and inner surfaces, is equal to 217 HV₁₀ (225 HV₁₀).

The minimum and maximum yield strength values were equal to 506 MPa and 534 MPa, respectively.

The minimum and maximum tensile strength value were equal to 601 and 611 MPa, respectively.

The minimum and maximum elongation % after rupture was 27% and 33%. (round specimen).

The average impact energy at −40° C. was 382 J, with a minimum value of 278 J. The average shear area was 98% with a minimum shear area of 85%.

The 50% FATT was around −60° C.

Hydrogen Induced cracking tests passed with CLR %=0%, CTR %=0% and CSR=0%.

Four point bend tests at 90% of AYS passed with no failures after 720 h of tests.

This steel pipe satisfies the grade X70Q.

Example 11

Steel pipes having outer diameter 323.9 mm and wall thickness of 25 mm, made according to the procedure described in example 3, were selected to manufacture Q&T bends of the same wall thickness.

The following chemical composition was used:

-   -   0.075% C, 1.01% Mn, 0.27% Si, 0.38% Cr, 0.30% Ni, 0.33% Mo,         0.031% Al, 0.0010% Ca, 0.024% Nb, 0.005% Ti, 0.003% V, 0.0047%         N, the remaining being iron and impurities; said impurities         being 0.09% Cu, 0.001% S, 0.011% P, 0.0002% B.     -   and being P1=14.2; P2=2.50; CE_(IIW)=0.41%; and CE_(PCM)=0.19%.

The steel pipe were subjected to the following steps:

-   -   hot induction bending at a temperature comprised between 800 and         870° C. and subjected to a bending rate comprised between 10 and         25 mm/min. The bends were manufactured with radius equal to         three times the outer diameter and tangent length of 1 m;     -   heating the bend, with a heating rate of 0.15° C./s, to an         austenitizing temperature of about 920° C. and providing a         soaking time of about 600 s;     -   quenching in a tank, achieving a cooling rate of about 20° C./s         at mid thickness in the bend body and a cooling rate of about         150° C./s in proximity of the outer and inner surfaces of the         pipe, in particular at 1.5-2 mm depth from said surfaces;     -   heating the bend, with a heating rate of 0.05° C./s, to a         tempering temperature of about 660° C. and providing a holding         time of about 600 sec at said tempering temperature.

The resulting average microstructure of the steel pipe comprises, in volume percentage:

-   -   at mid thickness, tempered bainite equal to about 75% and         ferrite (V_(F)) equal to about 25%,     -   at a distance up to 2 mm starting from outer and inner surfaces         of the steel pipe, tempered martensite equal to about 60% and         tempered bainite equal to about 40%.

The average prior austenite grain size, measured according to ASTM E112, is equal to 20 μm. The average packet size is equal to 6.5 μm.

The maximum hardness value, measured at 1.5-2.0 mm depth from the outer and inner surfaces, is equal to 230 HV₁₀ (<235 HV₁₀).

The minimum and maximum yield strength values were 518 MPa and 539 MPa respectively.

The minimum and maximum tensile strength values were 611 MPa and 621 MPa respectively.

The minimum and maximum elongation % after rupture were 28.0% and 30.0%, respectively.

The average impact energy at −60° C. was 287 J with a minimum value of 274 J and an average shear area of 100%.

The average 50% FATT was at about −90° C.

Hydrogen Induced cracking tests passed with CLR %=0%, CTR %=0% and CSR %=0%.

Four point bend tests at 90% of SMYS passed with no failures after 720 h of tests.

This steel pipe bend satisfies the grade X70Q.

Example 12

A steel with the following chemical composition has been selected:

-   -   0.076% C, 1.10% Mn, 0.26% Si, 0.35% Cr, 0.25% Ni, 0.25% Mo,         0.025% Al, 0.0010% Ca, 0.025% Nb, 0.0045% N, the remaining being         iron;     -   and being P1=13.6; P2=2.53; CE_(IIW)=0.40%; and CE_(PCM)=0.18%.

A seamless steel pipe has been hot formed, having a wall thickness of 22 mm.

Said hot formed steel pipe has been subjected to the following steps:

-   -   cooling the steel pipe in air, preferably still air, up to reach         the room temperature;     -   heating the steel pipe, with a heating rate of 0.35° C./s, to an         austenitizing temperature of 920° C. and providing a soaking         time of 900 s;     -   quenching in a tank, achieving a cooling rate of about 45° C./s         at mid thickness and a cooling rate of about 120° C./s in         proximity of the outer and inner surfaces of the pipe, in         particular at 1.5-2 mm depth from said surfaces;     -   heating the steel pipe, with a heating rate of 0.15° C./s, to a         tempering temperature of 650° C. and providing a holding time of         3600 sec at said tempering temperature.

The resulting average microstructure of the steel pipe comprises, in volume percentage:

-   -   at mid thickness, tempered bainite equal to about 85% and         ferrite equal to about 15%;     -   at a distance up to 2 mm starting from outer and inner surfaces         of the steel pipe, tempered martensite equal to about 15%,         tempered bainite equal to about 80% and ferrite equal to about         5%.

The average prior austenite grain size, measured according to ASTM E112, is equal to 16-18 μm.

The maximum hardness value, measured at 1.5-2.0 mm depth from the outer and inner surfaces, is equal to 220 HV₁₀ (<225 HV₁₀).

The minimum and maximum yield strength values were equal to 491 MPa and 497 MPa, respectively.

The minimum and maximum tensile strength value were equal to 589 and 595 MPa, respectively.

The minimum and maximum elongation % after rupture was 27% and 31%. (round specimen).

The average impact energy at −40° C. was 375 J, with a minimum value of 315 J. The average shear area was 100%.

The 50% FATT was around −80° C.

Hydrogen Induced cracking tests passed with CLR %=0%, CTR %=0% and CSR=0%.

Four point bend tests at 90% of AYS passed with no failures after 720 h of tests.

This steel pipe satisfies the grades X65Q, X60Q and X70Q.

From the foregoing description, it will be appreciated that inventive material and methods of manufacturing have been disclosed. While several components, techniques and aspects have been described with a certain degree of particularity, it is manifest that many changes can be made in the specific designs, constructions and methodology herein above described without departing from the spirit and scope of this disclosure.

Certain features that are described in this disclosure in the context of separate implementations can also be implemented in combination in a single implementation. Conversely, various features that are described in the context of a single implementation can also be implemented in multiple implementations separately or in any suitable subcombination. Moreover, although features may be described above as acting in certain combinations, one or more features from a claimed combination can, in some cases, be excised from the combination, and the combination may be claimed as any subcombination or variation of any subcombination.

Moreover, while methods may be depicted in the drawings or described in the specification in a particular order, such methods need not be performed in the particular order shown or in sequential order, and that all methods need not be performed, to achieve desirable results. Other methods that are not depicted or described can be incorporated in the example methods and processes. For example, one or more additional methods can be performed before, after, simultaneously, or between any of the described methods. Further, the methods may be rearranged or reordered in other implementations. Also, the separation of various system components in the implementations described above should not be understood as requiring such separation in all implementations, and it should be understood that the described components and systems can generally be integrated together in a single product or packaged into multiple products. Additionally, other implementations are within the scope of this disclosure.

Conditional language, such as “can,” “could,” “might,” or “may,” unless specifically stated otherwise, or otherwise understood within the context as used, is generally intended to convey that certain embodiments include or do not include, certain features, elements, and/or steps. Thus, such conditional language is not generally intended to imply that features, elements, and/or steps are in any way required for one or more embodiments.

Conjunctive language such as the phrase “at least one of X, Y, and Z,” unless specifically stated otherwise, is otherwise understood with the context as used in general to convey that an item, term, etc. may be either X, Y, or Z. Thus, such conjunctive language is not generally intended to imply that certain embodiments require the presence of at least one of X, at least one of Y, and at least one of Z.

Language of degree used herein, such as the terms “approximately,” “about,” “generally,” and “substantially” as used herein represent a value, amount, or characteristic close to the stated value, amount, or characteristic that still performs a desired function or achieves a desired result. For example, the terms “approximately”, “about”, “generally,” and “substantially” may refer to an amount that is within less than or equal to 10% of, within less than or equal to 5% of, within less than or equal to 1% of, within less than or equal to 0.1% of, and within less than or equal to 0.01% of the stated amount.

Some embodiments have been described in connection with the accompanying drawings. The FIGURE is drawn to scale, but such scale should not be limiting, since dimensions and proportions other than what are shown are contemplated and are within the scope of the disclosed inventions. Distances, angles, etc. are merely illustrative and do not necessarily bear an exact relationship to actual dimensions and layout of the devices illustrated. Components can be added, removed, and/or rearranged. Further, the disclosure herein of any particular feature, aspect, method, property, characteristic, quality, attribute, element, or the like in connection with various embodiments can be used in all other embodiments set forth herein. Additionally, it will be recognized that any methods described herein may be practiced using any device suitable for performing the recited steps.

While a number of embodiments and variations thereof have been described in detail, other modifications and methods of using and medical applications for the same will be apparent to those of skill in the art. Accordingly, it should be understood that various applications, modifications, materials, and substitutions can be made of equivalents without departing from the unique and inventive disclosure herein or the scope of the claims. 

What is claimed is:
 1. A seamless quenched and tempered steel pipe comprising: a yield strength from 415 MPa to 635 MPa and a wall thickness WT higher than or equal to 6 mm and lower than 35 mm; wherein the steel pipe has a chemical composition consisting of: 0.050-0.090 wt % C; 0.80-1.65 wt % Mn; 0.10-0.45 wt % Si; 0.10-0.60 wt % Cr; 0.05-0.45 wt % Ni; 0.05-0.40 wt % Mo; 0.020-0.040 wt % Al; 0.0030-0.0090 wt % N; 0.0008-0.0050 wt % Ca; 0.000-0.040 wt % Nb; 0.000-0.020 wt % Ti; 0.000-0.070 wt % V; 0.000-0.030 wt % Zr; 0.000-0.030 wt % Ta; 0.00-0.25 wt % Cu; 0.000-0.003 wt % S; 0.000-0.018 wt % P; and 0.0000-0.0005 wt % B; the remainder being Fe; wherein at least one of Nb and V is present, (V+Nb) content being lower than 0.07 wt %; wherein, defining a first parameter: P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]+50×(V+Nb), the chemical composition satisfies a first condition 10≦P1≦14.5; wherein the quenched and tempered steel pipe has, at mid thickness, a microstructure comprising, in volume percentage, tempered bainite greater than or equal to 40% and ferrite (V_(F)) lower than or equal to 60%, and has at a distance up to 2 mm, starting from the outer surface, a microstructure comprising, in volume percentage, tempered martensite lower than 70%, tempered bainite higher than 30% and traces of ferrite less than or equal to 10%; wherein the microstructure of the quenched and tempered steel pipe has an average prior austenite grain size, measured by ASTM Standard E112, smaller than 25 μm; and wherein the maximum hardness values, measured at 1.5-2.0 mm depth from the outer and inner surfaces, are not higher than 235 HV₁₀.
 2. The seamless quenched and tempered steel pipe of claim 1, wherein, defining a second parameter P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V), the chemical composition satisfies a second condition P2≧2.00.
 3. The seamless quenched and tempered steel pipe of claim 2, wherein the second condition, as a function of grade and wall thickness (WT), is: grade WT < 20 mm 20 ≦ WT ≦ 35 mm X60 P2 ≧ 2.00 P2 ≧ 2.20 X65 P2 ≧ 2.10 P2 ≧ 2.30 X70 P2 ≧ 2.35  P2 ≧ 2.45.


4. The seamless quenched and tempered steel pipe of claim 1, wherein, at a distance up to 2 mm starting from the outer surface of the steel pipe, the microstructure comprises of tempered martensite lower than 40% and tempered bainite higher than 60%.
 5. The seamless quenched and tempered steel pipe of claim 1, wherein, at a distance up to 2 mm starting from the outer surface of the steel pipe, the microstructure comprises tempered martensite lower than 20% and tempered bainite higher than 80%.
 6. The seamless quenched and tempered steel pipe of claim 1, wherein, at mid thickness, the microstructure comprises tempered bainite greater than or equal to 50% and ferrite (V_(F)) lower than or equal to 50%.
 7. The seamless quenched and tempered steel pipe of claim 1, wherein, at mid thickness, the microstructure comprises tempered bainite greater than or equal to 80% and ferrite (V_(F)) lower than or equal to 20%.
 8. The seamless quenched and tempered steel pipe of claim 1, wherein the (V+Nb) content is lower than 0.055 wt %.
 9. The seamless quenched and tempered steel pipe of claim 1, wherein, at mid thickness, the microstructure comprises ferrite (V_(F)) lower than or equal to 60% for a pipe of grade X60, ferrite (V_(F)) lower than or equal to 40% for a pipe of grade X65, ferrite (V_(F)) lower than or equal to 20% for a pipe of grade X70.8.
 10. The seamless quenched and tempered steel pipe of claim 1, wherein: should be ti CE _(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 is in the range of 0.26% to 0.43%, and CE _(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B is in the range of 0.14% to 0.22%.
 11. The seamless quenched and tempered steel pipe of claim 1, wherein the chemical composition consists of: 0.050-0.090 wt % C; 0.90-1.35 wt % Mn; 0.10-0.35 wt % Si; 0.10-0.40 wt % Cr; 0.05-0.40 wt % Ni; 0.07-0.40 wt % Mo; 0-0.070 wt % V; 0.020-0.040 wt % Al; 0.0008-0.0030 wt % Ca; 0.000-0.035 wt % Nb; 0.000-0.015 wt % Ti; 0.0030-0.0070 wt % N; 0.00-0.20 wt % Cu; 0.000-0.002 wt % S; 0.000-0.015 wt % P; 0.0000-0.0005 wt % B; 0.000-0.015 wt % Zr; and 0.000-0.015 wt % Ta; the remainder being Fe.
 12. The seamless quenched and tempered steel pipe of claim 11, wherein the chemical composition consisting of: 0.060-0.085 wt % C; 1.00-1.30 wt % Mn; 0.10-0.30 wt % Si; 0.20-0.40 wt % Cr; 0.20-0.40 wt % Ni; 0.10-0.35 wt % Mo; 0.000-0.070 wt % V; 0.020-0.040 wt % Al; 0.0015-0.0030 wt % Ca; 0.000-0.030 wt % Nb; 0.000-0.015 wt % Ti; 0.0030-0.0070 wt % N; 0.00-0.15 wt % Cu; 0.000-0.0015 wt % S; 0.000-0.012 wt % P; 0.0000-0.0005 wt % B; 0.000-0.010 wt % Zr; and 0.000-0.010 wt % Ta; the remainder being Fe.
 13. The seamless quenched and tempered steel pipe of claim 12, wherein the chemical composition consists of: 0.060-0.085 wt % C; 1.00-1.25 wt % Mn; 0.10-0.30 wt % Si; 0.30-0.40 wt % Cr; 0.25-0.35 wt % Ni; 0.25-0.35 wt % Mo; 0.000-0.040 wt % V; 0.020-0.035 wt % Al; 0.0010-0.0030 wt % Ca; 0.020-0.030 wt % Nb; 0.000-0.015 wt % Ti; 0.0030-0.0060 wt % N; 0.00-0.15 wt % Cu; 0.000-0.0015 wt % S; 0.000-0.011 wt % P; 0.0000-0.0005 wt % B; 0.000-0.010 wt % Zr; and 0.000-0.010 wt % Ta; the remainder being Fe.
 14. The seamless quenched and tempered steel pipe of claim 1, wherein the chemical composition consists of: 0.050-0.090 wt % C; 0.90-1.30 wt % Mn; 0.10-0.35 wt % Si; 0.10-0.25 wt % Cr; 0.08-0.30 wt % Ni; 0.08-0.15 wt % Mo; 0.000-0.045 wt % V; 0.020-0.040 wt % Al; 0.0008-0.0030 wt % Ca; 0.000-0.035 wt % Nb; 0.000-0.015 wt % Ti; 0.0030-0.0070 wt % N; 0.00-0.20 wt % Cu; 0.000-0.002 wt % S; 0.000-0.015 wt % P; 0.0000-0.0001 wt % B; 0.000-0.010 wt % Zr; and 0.000-0.010 wt % Ta; the remainder being Fe; and satisfies the following additional conditions: CE _(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range 0.26% to 0.37%; CE _(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.14% to 0.18%; P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]+50×(V+Nb) in the range of 10 to 14.5; and P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)≧2.0.
 15. The seamless quenched and tempered steel pipe of claim 1, wherein the chemical composition consists of: 0.060-0.090 wt % C; 0.95-1.30 wt % Mn; 0.10-0.35 wt % Si; 0.10-0.30 wt % Cr; 0.20-0.40 wt % Ni; 0.14-0.25 wt % Mo; 0.000-0.045 wt % V; 0.020-0.040 wt % Al; 0.0008-0.0030 wt % Ca; 0.000-0.035 wt % Nb; 0.000-0.015 wt % Ti; 0.0030-0.0070 wt % N; 0.00-0.20 wt % Cu; 0.000-0.002 wt % S; 0.000-0.015 wt % P; 0.0000-0.0001 wt % B; 0.000-0.010 wt % Zr; and 0.000-0.010 wt % Ta; the remainder being Fe; and satisfies the following additional conditions: CE _(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range 0.36% to 0.43%; CE _(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.18% to 0.21%; P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]+50×(V+Nb) in the range of 10 to 14.5; and P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)≧2.30.
 16. The seamless quenched and tempered steel pipe of claim 1, wherein the chemical composition consists of: 0.060-0.090 wt % C; 0.95-1.30 wt % Mn; 0.10-0.35 wt % Si; 0.20-0.40 wt % Cr; 0.25-0.40 wt % Ni; 0.25-0.35 wt % Mo; 0.000-0.010 wt % V; 0.020-0.040 wt % Al; 0.0008-0.0030 wt % Ca; 0.020-0.035 wt % Nb; 0.000-0.015 wt % Ti; 0.0030-0.0070 wt % N; 0.00-0.20 wt % Cu; 0.000-0.002 wt % S; 0.000-0.015 wt % P; 0.0000-0.0001 wt % B; 0.000-0.010 wt % Zr; and 0.000-0.010 wt % Ta; the remainder being Fe; and satisfies the following additional conditions: CE _(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range 0.37% to 0.43%; CE _(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.18% to 0.21%; P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]+50×(V+Nb) in the range of 10 to 14.5; and P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)≧2.30.
 17. The seamless quenched and tempered steel pipe of claim 1, wherein the chemical composition consists of: 0.060-0.090 wt % C; 0.90-1.20 wt % Mn; 0.10-0.35 wt % Si; 0.10-0.25 wt % Cr; 0.05-0.20 wt % Ni; 0.05-0.15 wt % Mo; 0.000-0.070 wt % V; 0.020-0.040 wt % Al; 0.0008-0.0030 wt % Ca; 0.000-0.005 wt % Nb; 0.005-0.015 wt % Ti; 0.0030-0.0090 wt % N; 0.00-0.20 wt % Cu; 0.000-0.003 wt % S; 0.000-0.015 wt % P; 0.0000-0.0001 wt % B; 0.000-0.010 wt % Zr; and 0.000-0.010 wt % Ta; the remainder being Fe; and satisfies the following additional conditions: CE _(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range 0.26% to 0.36%; CE _(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.14% to 0.18%; P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]+50×(V+Nb) in the range of 10 to 14.5; and P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)≧2.00.
 18. The seamless quenched and tempered steel pipe of claim 1, wherein the chemical composition consists of: 0.060-0.090 wt % C; 0.95-1.30 wt % Mn; 0.10-0.35 wt % Si; 0.10-0.40 wt % Cr; 0.05-0.40 wt % Ni; 0.07-0.25 wt % Mo; 0.000-0.070 wt % V; 0.020-0.040 wt % Al; 0.0008-0.0030 wt % Ca; 0.000-0.005 wt % Nb; 0.005-0.015 wt % Ti; 0.0030-0.0080 wt % N; 0.00-0.20 wt % Cu; 0.000-0.003 wt % S; 0.000-0.015 wt % P; 0.0000-0.0001 wt % B; 0.000-0.010 wt % Zr; and 0.000-0.010 wt % Ta; the remainder being Fe; and satisfies the following additional conditions: CE _(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range 0.31% to 0.41%; CE _(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.15% to 0.20%; P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]+50×(V+Nb) in the range of 11 to 14.5; and P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)≧2.30.
 19. The seamless quenched and tempered steel pipe of claim 1, wherein the chemical composition consists of: 0.060-0.090 wt % C; 1.00-1.30 wt % Mn; 0.10-0.35 wt % Si; 0.20-0.40 wt % Cr; 0.20-0.40 wt % Ni; 0.10-0.25 wt % Mo; 0.000-0.070 wt % V; 0.020-0.040 wt % Al; 0.0008-0.0030 wt % Ca; 0.000-0.005 wt % Nb; 0.005-0.015 wt % Ti; 0.0030-0.0070 wt % N; 0.00-0.15 wt % Cu; 0.000-0.003 wt % S; 0.000-0.012 wt % P; 0.0000-0.0001 wt % B; 0.000-0.010 wt % Zr; and 0.000-0.010 wt % Ta; the remainder being Fe; and satisfies the following additional conditions: CE _(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15 in the range 0.37% to 0.43%; CE _(PCM)=C+Si/30+Mn/20+Cr/20+Cu/20+Ni/60+Mo/15+V/10+5×B in the range of 0.16% to 0.22%; P1=(60×C)+Cr+[5×e ^((35×Mo/WT))]+50×(V+Nb) in the range of 12.5 to 14.5; and P2=(9×C)+(1.2×Mn)+Cr+(0.7×Mo)+(2×V)≧2.30.
 20. A method of manufacturing a seamless quenched and tempered steel pipe comprising: hot forming a seamless steel pipe having a wall thickness WT higher than or equal to 6 mm and lower than 35 mm and a chemical composition consisting of: 0.050-0.090 wt % C; 0.80-1.65 wt % Mn; 0.10-0.45 wt % Si; 0.10-0.60 wt % Cr; 0.05-0.45 wt % Ni; 0.05-0.40 wt % Mo; 0.020-0.040 wt % Al; 0.0030-0.0090 wt % N; 0.0008-0.0050 wt % Ca; 0.000-0.040 wt % Nb; 0.000-0.020 wt % Ti; 0.000-0.070 wt % V; 0.000-0.030 wt % Zr; 0.000-0.030 wt % Ta; 0.00-0.25 wt % Cu; 0.000-0.003 wt % S; 0.000-0.018 wt % P; and 0.0000-0.0005 wt % B; the remainder being Fe; cooling the seamless steel pipe in air down to reach room temperature; heating the seamless steel pipe, with a first heating rate between 0.1° C./s and 10° C./s, to an austenitizing temperature above the Ac3 transformation point, in a range between 880° C. and 980° C., and providing a soaking time between 180s and 5400s; quenching the seamless steel pipe with a cooling rate in the range of 20 to 80° C./s at mid thickness of the pipe, or at mid thickness and at the inner surface of the pipe, and with a cooling rate of 100-200° C./s in proximity of the outer and inner surfaces of the pipe or in proximity of the outer surface only; and heating the seamless steel pipe, with a second heating rate between 0.1° C./s and 10° C./s, to a tempering temperature comprised in a predetermined range, and providing a holding time at said tempering temperature between 600s and 7200s; wherein said predetermined range is calculated with a tolerance of ±20° C. using the following equation: ${T\left( {{^\circ}\mspace{14mu}{C.}} \right)} = {\frac{1000 \times \left( {0.82 + C + {4.5 \times {Cr}} + {11.5 \times {Mo}} + {25 \times V}} \right)}{a - {3.8 \times C} + {4.3 \times {Cr}} + {10.6 \times {Mo}} + {22 \times V}} - 273.15}$  where a is a parameter whose value is 1.75, 1.90 or 2.15 if the grade to be achieved is the X60, X65 or X70, respectively; and wherein the final steel pipe has a yield strength from 415 MPa to 635 MPa.
 21. The method of claim 20, wherein heating occurs in gas-fired furnace, provided with at least one burner, in which the oxygen concentration is less than 10%.
 22. The method of claim 21, wherein the oxygen concentration is in the range of 0.5% to 4%.
 23. The method of claim 21, wherein at an exit from the gas-fired furnace the pipe is immediately descaled by high pressure water and moved in less than 120 s in a water quenching system.
 24. A pipe bend, obtained by a seamless steel pipe of claim 1, having maximum hardness values, measured at 1.5 mm to 2 mm depth from the surface, not higher than 235 HV₁₀.
 25. The pipe bend of claim 24, having maximum hardness values, measured at 1.5 mm to 2 mm depth from the surface, not higher than 230 HV₁₀.
 26. The seamless quenched and tempered steel pipe of claim 1, wherein the microstructure has, at a distance up to 2 mm, starting from the inner surface of the pipe, a microstructure comprising, in volume percentage, tempered martensite lower than 70%, tempered bainite higher than 30% and traces of ferrite less than or equal to 10%. 